Continuous and Short Fiber Reinforced Composite in Root Post-Core System of Severely Damaged Incisors

PURPOSE The aim of this study was to determine the static load-bearing capacity of endodontically treated maxillary incisors restored with post-core complex made of experimental fiber composite resin (FC) and complete crown made of particulate filler composite (PFC). Further aim was to evaluate the effect of FC resin on the failure mode of the restoration. MATERIAL AND METHODS The experimental composite resin (FC) was prepared by mixing 22.5 wt% of short E-glass fibers (3 mm in length) and 22.5 wt% of semi-interpenetrating polymer network (IPN) resin with 55 wt% of silane treated silica fillers. Thirty extracted sound upper central incisors were used. Twenty teeth were prepared by cutting the clinical crown 2 mm above the cemento-enamel junction horizontally. Restorations were made by two techniques (n=10). Group A (control group) contained samples of sound incisor teeth. Group B had teeth restored using glass fiber post (everStick, Stick- Teck) and PFC (Filtek Z250, 3M-ESPE) to build up core and complete crown. In Group C, the teeth were restored with FC as post-core and complete crown of PFC. The root canals were prepared and posts were cemented with a dual cure resin cement. The restorations were polymerized with a hand-light curing unit. All restored teeth were stored in water at room temperature for 24 h before they were statically loaded with speed of 1.0 mm/min until fracture. Data were analyzed using ANOVA (p=0.05). Failure modes were visually examined. RESULTS ANOVA revealed that restored incisors (Group B and C) had a statistically significantly lower load-bearing capacity (p<0.05) than the control group. Restorations made from FC post-core and PFC coverage (Group C) gave force value of 363 N (112 SD), which was higher than the value of Group B (211 N, 50 SD). CONCLUSIONS Within the limitations of this study, the teeth restored with experimental fiber composite post-core demonstrated higher load bearing capacity than those with fiber post and PFC core.