Investigation of secondary hardening in Co–35Ni–20Cr–10Mo alloy using analytical scanning transmission electron microscopy
نویسندگان
چکیده
The mechanism of secondary hardening in MP35N (Co–35Ni–20Cr–10Mo) alloy due to exposures at elevated temperatures has been studied. It was observed that short exposure to elevated temperatures increased the ultimate tensile strength and yield stress while decreasing the elongation of MP35N wires. Upon aging at temperatures from 300 to 900 C the elastic modulus increased although no changes in crystallographic orientation or microstructure were observed. The grain size and major texture components were unchanged following aging. Analytical scanning transmission electron microscope investigation showed that MP35N is hardened by preferential segregation of molybdenum to stacking faults and deformation twins. It also revealed that the concentration of molybdenum segregation was proportional to the amount of initial cold work before aging. 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
منابع مشابه
Investigation of early stage deformation mechanisms in a metastable β titanium alloy showing combined TWIP and TRIP effects
As expected from the alloy design procedure, combined Twinning Induced Plasticity (TWIP) and Transformation Induced Plasticity (TRIP) effects are activated in a metastable β Ti-12(wt.%)Mo alloy. In-situ Synchrotron X-ray diffraction (XRD), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) observations were carried out to investigate the deformation mechanisms an...
متن کاملEffect of Aging Condition on Semisolid Cast 2024 Aluminum Alloy
2024 Aluminum alloy was squeezed cast by the Gas Induced Semi Solid (GISS) process. Effect of artificial aging on microstructure and mechanical properties of this alloy was studied in the present work. The solutionized specimens were aged hardened at temperatures of 175°C, 200°C, and 225°C under various time durations. The highest hardness of about 77.7 HRE was attained from specimen aged at th...
متن کاملAn Analytical Electron Microscopy Study of Paraequilibrium Cementite Precipitation in Ultra-High-Strength Steel
To support quantitative design of ultra-high-strength (UHS) secondary-hardening steels, the precipitation of cementite prior to the precipitation of the M2C phase is investigated using a model alloy. The microstructure of cementite is investigated by transmission electron microscopy (TEM) techniques. Consistent with earlier studies on tempering of Fe-C martensite, lattice imaging of cementite s...
متن کاملRelationship between Microstructure and Properties of Cu-Cr-Ag-(Ce) Alloy Using Microscopic Investigation
Microstructure, precipitation hardening response, and mechanical and physical properties of Cu-Cr-Ag alloy and Cu-Cr-Ag-Ce alloy have been investigated using transmission electron microscopy, scanning electron microscope, optical microscope, electrical conductivity analysis, and tensile test. The influence of element Ce on the matrix refinement, impurity removal, and precipitation in the Cu-Cr-...
متن کاملAbnormal Plastic Behavior of Fine Grain Mp35n Alloy During Room Temperature Tensile Testing
In this paper, results of an investigation on the strain hardening responses of superalloy MP35N with two average grain sizes of 38 and 1 μm, during room temperature tensile testing are reported. The microstructural evolution of the deformed samples was studied using optical and transmission electron microscopy (TEM) techniques. The strain hardening behavior of the 38 μm material was rather sim...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2013