Excellent Biofouling Alleviation of Thermoexfoliated Vermiculite Blended Poly(ether sulfone) Ultrafiltration Membrane.

نویسندگان

  • Yasin Orooji
  • Feng Liang
  • Amir Razmjou
  • Sha Li
  • Mohammad Reza Mofid
  • Quan Liu
  • Kecheng Guan
  • Zhengkun Liu
  • Wanqin Jin
چکیده

Flux and antifouling properties of mixed matrix membranes (MMMs) are yet to attain satisfactory status. The objective of this study is to find a method for mitigating the biofouling of poly(ether sulfone) (PES) ultrafiltration membranes via blending of thermoexfoliated vermiculite (VMT). Flow cytometry analysis shows that the behaviors of Bacillus subtilis 168 as a Gram-positive bacterium and Escherichia coli DH5 alpha as a Gram-negative bacterium were different. Hence, cell property is a suspected contributory factor in biofilm formation. Accordingly, considering the local predominant bacterial strains, a regionally customized membrane could scientifically be an expert solution for biofouling mitigation. Fabricated composite membranes have shown a higher flux compared to control PES membrane. Among all composite membranes, the PES-VMT0.10 had the highest flux of 476.4 L/(m2 h) (LMH) before fouling, and the highest flux of 210.7 LMH after three cycles of usage. In addition, the rejection rate of the PES-VMT0.15 The bovine serum albumin (BSA) sample was >77%, while that of the PES-VMT0.10 was >84%. The results of the static BSA adsorption test and the bacterial attachment test indicated that the membranes with macro-roughness on their surface showed better antibiofouling resistance. The antifouling properties of the modified membranes were also improved, because of their optimal wettability. On one hand, the hydrophilicity of membranes caused damaging both Gram-positive and Gram-negative bacteria and bacteriocidal effect. On the other hand, BSA adsorption and bacterial attachment on the membrane surface were affected by pore diameter.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Tailoring the Characteristics of Poly (phenylene-ether-ether) sulfone Membrane for Efficient Glycerol/Biodiesel Separation

Poly (phenylene-ether-ether) sulfone membrane was fabricated and characterized by efficient glycerol/biodiesel separation produced from waste cooking oils trans-esterification. The membrane preparation was processed by phase inversion technique. The morphology, Physico-chemical properties and separation behavior of membranes were studied at various PPEES concentration. A uniform surface was...

متن کامل

A novel guanidinium grafted poly(aryl ether sulfone) for high-performance hydroxide exchange membranes.

A novel poly(aryl ether sulfone) ionomer containing hexaalkylguanidinium groups was synthesized, and membranes formed from this polymer displayed large ionic clusters, high hydroxide conductivity, and excellent solubility in low boiling point water-soluble solvents such as ethanol and methanol.

متن کامل

Recovery of valuable soluble compounds from washing waters generated during small fatty pelagic surimi processing by membrane processes.

This work focuses on the treatment of washing waters coming from surimi manufacturing using ultrafiltration technology at a laboratory scale. Four membrane materials (poly-ether sulfone, polyacrilonytrile, poly vinylidene fluoride and regenerated cellulose) and 5 Molecular Weight Cut-Off (from 3 to 100 kDa) have been studied at bench laboratory scale using the pilot Rayflow 100, commercialised ...

متن کامل

Preparation of blend hydrophilic PSF-SPEEK ultrafiltration membranes for oily wastewater treatment

Membrane separation is known as an efficient technique for the oily wastewater treatment. Therefore, in the present study, sulfonated poly (ether ether ketone) (SPEEK) was introduced into the polysulfone (PSF) solution in order to enhance the hydrophilicity and the membrane structure for the oil–water separation. The hollow fiber membranes were fabricated via a phase-inversion process. The memb...

متن کامل

Short-term adhesion and long-term biofouling testing of polydopamine and poly(ethylene glycol) surface modifications of membranes and feed spacers for biofouling control.

Ultrafiltration, nanofiltration membranes and feed spacers were hydrophilized with polydopamine and polydopamine-g-poly(ethylene glycol) surface coatings. The fouling propensity of modified and unmodified membranes was evaluated by short-term batch protein and bacterial adhesion tests. The fouling propensity of modified and unmodified membranes and spacers was evaluated by continuous biofouling...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • ACS applied materials & interfaces

دوره 9 35  شماره 

صفحات  -

تاریخ انتشار 2017