Preparation of Cu36Zr48Ag8Al8 Bulk Metallic Glass with a Diameter of 25mm by Copper Mold Casting
نویسندگان
چکیده
The Cu36Zr48Ag8Al8 alloy exhibits very high glass-forming ability. We have succeeded in synthesizing a Cu36Zr48Ag8Al8 bulk glassy alloy with a diameter of 25mm using the conventional copper mold injection casting. The absence of a crystalline phase was confirmed by X-ray diffraction and differential scanning calorimetry examinations. The critical cooling rate for formation of a glassy phase for the Cu36Zr48Ag8Al8 alloy was estimated to be less than 6.4K/s. High glass-forming ability and high strength might contribute to its commercial application for the Cu36Zr48Ag8Al8 bulk metallic glass. [doi:10.2320/matertrans.48.629]
منابع مشابه
Glass Forming Ability and Corrosion Resistance of Zr-Cu-Ni-Al-Ag Bulk Metallic Glass
Zr70−xCu12.5Ni10Al7.5Agx (x = 0–10) bulk metallic glasses (BMGs) have been prepared by copper mold casting. The glass-forming ability (GFA) and corrosion behavior of Zr-based BMGs have been investigated. It is found that the GFA of Zr-based BMGs first increases and then decreases with the increase of the Ag content, and the best glass former is Zr65Cu12.5Ni10Al7.5Ag5 with the maximum thickness ...
متن کاملStrain rate induced crystallization in bulk metallic glass-forming liquid.
We report on the solidification of Au49, Ag5.5, Pd2.3, Cu26.9, Si16.3 bulk metallic glass under various strain rates. Using a copper mold casting technique with a low strain rate during solidification, this alloy is capable of forming glassy rods of at least 5 mm in diameter. Surprisingly, when the liquid alloy is splat cooled at much higher cooling rates and large strain rates, the solidified ...
متن کاملBulk Glassy and Quasicrystalline (Zr65Al7:5Cu27:5)100 xTix Alloys and Their Mechanical Properties
The glass-forming ability (GFA) and thermal stability of (Zr65Al7:5Cu27:5)100 xTix (x 1⁄4 0 15; in at%) alloys have been investigated. It was revealed that a certain amount of Ti addition could improve the GFA of Zr65Al7:5Cu27:5 alloy effectively. The best bulk metallic glass (BMG) forming composition was found at (Zr65Al7:5Cu27:5)93Ti7. Bulk glassy samples with diameter of 7mm were made by mea...
متن کاملFormation of Bulk Pd-Cu-Si-P Glass with Good Mechanical Properties
Glassy Pd85 xCuxSi10P5 (x 1⁄4 5{12 at%) alloys with a supercooled liquid region ( Tx) of 51–73K were synthesized despite the low metalloid content. The glassy Pd79Cu6Si10P5 alloy exhibits the largest Tx of 73K in the present alloy system and its critical diameter for glass formation reaches 5mm by copper mold casting. For the bulk glassy Pd79Cu6Si10P5 alloy, the Young’s modulus, compressive yie...
متن کاملEVALUATION OF PRESSURE EFFECT ON HEAT TRANSFER COEFFICIENT AT THE METAL- MOLD INTERFACE FOR CASTING OF A356 AL ALLOY
Abstract: During solidification and casting in metallic molds, the heat flow is controlled by the thermal resistance at the casting-mold interface. Thus heat transfer coefficient at the metal- mold interface has a predominant effect on the rate of heat transfer. In some processes such as low pressure and die-casting, the effect of pressure on molten metal will affect the rate of heat transfer a...
متن کامل