Porous Titanium Scaffolds Produced by Powder Metallurgy for Biomedical Applications
نویسندگان
چکیده
Department of Bioscience and Buccal Diagnosis, São Jose dos Campos School of Dentistry, State University of São Paulo – UNESP, Av. Engenheiro Francisco José Longo, 777, 12245-000 São José dos Campos SP, Brazil National Institute of Technology, Av. Venezuela, 200, Centro, Rio de Janeiro RJ, Brazil Department of Materials, Air and Space Institute, CTA, Praça Mal. do Ar Eduardo Gomes, 14, 12904-000 São José dos Campos SP, Brazil
منابع مشابه
Microstructure, in Vitro Corrosion and Mechanical Properties of porous Magnesium-Zinc Nanocomposite Scaffolds
Due to good biocompatibility, corrosion and mechanical properties, magnesium (Mg) is considered promising degradable material for orthopedic applications. In this work, Mg-MgZnx (x= 1, 2, 3 and 4) nanocomposites scaffolds with different porosities were synthesized via powder metallurgy method. The microstructure, composition, in vitro corrosion and mechanical properties of porous magnesium-zinc...
متن کاملPorous, Superelastic NiTi Produced by Powder-Metallurgy
Near-stoichiometric NiTi was foamed in the solid state at elevated temperatures through creep expansion of highpressure argon pores previously entrapped during powder consolidation. A sample with 17% porosity was found to be superelastic up to a compressive stress of 800 MPa.
متن کاملPorous Structure Characterization in Titanium Coating for Surgical Implants
Powder metallurgy techniques have been used to produce controlled porous structures, such as the porous coatings applied for dental and orthopedic surgical implants, which allow bony tissue ingrowth within the implant surface improving fixation. This work presents the processing and characterization of titanium porous coatings of different porosity levels, processed through powder metallurgy te...
متن کاملBiocompatibility of Advanced Manufactured Titanium Implants—A Review
Titanium (Ti) and its alloys may be processed via advanced powder manufacturing routes such as additive layer manufacturing (or 3D printing) or metal injection moulding. This field is receiving increased attention from various manufacturing sectors including the medical devices sector. It is possible that advanced manufacturing techniques could replace the machining or casting of metal alloys i...
متن کاملTitanium Powder Sintering in a Graphite Furnace and Mechanical Properties of Sintered Parts
Recent accreditation of titanium powder products for commercial aircraft applications marks a milestone in titanium powder metallurgy. Currently, powder metallurgical titanium production primarily relies on vacuum sintering. This work reported on the feasibility of powder sintering in a non-vacuum furnace and the tensile properties of the as-sintered Ti. Specifically, we investigated atmospheri...
متن کامل