Application of Carbon Based Nano-Materials to Aeronautics and Space Lubrication

The tribology program at NASA Glenn Research Center in Cleveland, Ohio, is investigating carbon based nano-particles for their potential in advanced concept lubrication products. Service conditions range from high temperature atmospheric to low temperature vacuum. Some of the lubricants and surface coatings of tribological significance that we have evaluated include neat nano-particles, both grown insitu and as bulk material deposited on the substrate, and nano-particles dispersed in oils which are all highly substrate interactive. We discuss results of testing these systems in a spiral orbit tribometer (SOT) and a unidirectional pin-on-disc (PoD) tribometer. A Nano-onions/Krytox mixture evaluated as a lubricant for angular contact bearings in air caused a marked lowering of the coefficient of friction (CoF) (0.04 to 0.05) for the mixture with an eight-fold improvement in lifetime over that of the Krytox alone. In vacuum, no effect was observed from the nanoonions. Multi-walled nanotubes (MWNT) and graphitized MWNT were tested under sliding friction in both air and vacuum. The MWNT which were grown in-situ oriented normal to the sliding surface exhibited low CoF (0.04) and long wear lives. Bulk MWNT also generate low CoF (0.01 to 0.04, vacuum; and 0.06, air) and long wear life (>1 million orbits, vacuum; and >3.5 million, air). Dispersed GMWNT were superior to MWNT and both were superior to aligned MWNT indicating that orientation is not an issue for solid lubrication. Single-walled nanotubes (SWNT) were modified by cutting into shorter segments and by fluorination. All SWNTs exhibited low CoF in air, with good wear lives. The SWNT with slight fluorination yielded an ultra-low CoF of 0.002 although the best wear life was attributed to the nascent SWNT.