Deactivation Mechanism of Fe/Zeolite Catalysts by C3H6 Coking for Selective Catalytic Reduction of NO with Ammonia
نویسندگان
چکیده
Various Fe-Zeolite catalysts N O c o n v e r s i o n / % Initial activiy After HC coking 30 min Junhua Li*, Ralph T. Yang, Yuhe Wang, Yisun Cheng 3 , Christine K. Lambert Department of Chemical Engineering, University of Michigan, Ann Arbor, MI 48109, (USA) Department of Environment Science and Engineering, Tsinghua University, Beijing, (China) Research & Innovation Center, Ford Motor Company * [email protected]; [email protected]
منابع مشابه
Mesoporous Fe-containing ZSM-5 zeolite single crystal catalysts for selective catalytic reduction of nitric oxide by ammonia
Mesoporous and conventional Fe-containing ZSM-5 catalysts (0.5–8 wt% Fe) were prepared using a simple impregnation method and tested in NO selective catalytic reduction (SCR) with NH3. It was found that mesoporous Fe-ZSM-5 catalysts exhibit higher SCR activities than comparable conventional catalysts. Furthermore, conventional Fe-ZSM-5 catalysts have maximum activity at ~ 2.5 wt% Fe while for t...
متن کاملMössbauer and Magnetic Studies of Iron-Zeolite and Iron-Cobalt Zeolite Catalysts Used in Synthesis Gas Conversion
Medium-pore (diameter ~ 6A) zeolites such as ZSM-5 and silicalite impregnated with Group VIII metals provide selective catalytic pathways for the conversion of synthesis gas to gasoline or olefins. Mössbauer and magnetic studies on these catalysts containing iron or iron plus cobalt are reported. The zeolites were impregnated with metal nitrate solutions, reduced, and carbided to yield showed F...
متن کاملHeterogeneous Catalyst Deactivation and Regeneration: A Review
Deactivation of heterogeneous catalysts is a ubiquitous problem that causes loss of catalytic rate with time. This review on deactivation and regeneration of heterogeneous catalysts classifies deactivation by type (chemical, thermal, and mechanical) and by mechanism (poisoning, fouling, thermal degradation, vapor formation, vapor-solid and solid-solid reactions, and attrition/crushing). The key...
متن کاملThe Effect of Coking on Kinetics of HDS Reaction under Steady and Transient States
A study was made of the coking of a commercial fresh sulfide Ni-Mo/Al2O3 catalyst in a fixed-bed reactor. The catalyst was coked using different coke precursors in the gas oil under accelerated conditions at temperatures of 400 to 450°C to yield different deactivated catalysts containing 2-20 wt% C. Two cases were studied; crushed catalyst without diffusional ...
متن کاملFacile Synthesis of a Novel Hierarchical ZSM‐5 Zeolite: A Stable Acid Catalyst for Dehydrating Glycerol to Acrolein
Catalytic biomass conversion is often hindered by coking. Carbon compounds cover active surface and plug pores, causing catalyst deactivation. Material design at the nanoscale allows tailoring of the catalytic activity and stability. Here, we report a simple synthesis of nanosized ZSM-5 materials by using a silicalite-1 seeding suspension. ZSM-5 crystals were grown from a deionized silica sourc...
متن کامل