Literature Review: Theory and Application of In-Line Inspection Technologies for Oil and Gas Pipeline Girth Weld Defection
نویسندگان
چکیده
Girth weld cracking is one of the main failure modes in oil and gas pipelines; girth weld cracking inspection has great economic and social significance for the intrinsic safety of pipelines. This paper introduces the typical girth weld defects of oil and gas pipelines and the common nondestructive testing methods, and systematically generalizes the progress in the studies on technical principles, signal analysis, defect sizing method and inspection reliability, etc., of magnetic flux leakage (MFL) inspection, liquid ultrasonic inspection, electromagnetic acoustic transducer (EMAT) inspection and remote field eddy current (RFDC) inspection for oil and gas pipeline girth weld defects. Additionally, it introduces the new technologies for composite ultrasonic, laser ultrasonic, and magnetostriction inspection, and provides reference for development and application of oil and gas pipeline girth weld defect in-line inspection technology.
منابع مشابه
Engineering Critical Assessment for Offshore Pipeline with Semi Elliptical Surface Cracks in Girth Weld – Comparison of FEM and BS7910 Guideline
Economical design with sufficient fracture resistance is of high importance in any offshore pipeline projects. Using an Engineering Critical Assessment (ECA), alternate acceptance criteria for pipeline girth weld inspection can significantly reduce the cost of constructing of offshore oil and gas pipeline by minimizing unnecessary repairs. Offshore pipelines consist of short pipeline segments c...
متن کاملExperimental Study of the Residual Stresses in Girth Weld of Natural Gas Transmission Pipeline
In order to achieve integrated condition in the girth welding of high pressure natural gas transmission pipelines, the weld zones and its surrounding area should have good mechanical properties. Residual stresses are an important defect especially in the girth welding of the pipeline. In this study, two API X70 steel pipes (with spiral seam weld) of 56 inches outside diameter and 0.780 inch wal...
متن کاملINVESTIGATING THE EFFECT OF CRACK GEOMETRIES AND WELD MISMATCHING IN ORDER TO OPTIMIZE ECA ANALYSIS OF GIRTH WELDED OFFSHORE PIPELINES
Offshore pipelines are an effective tool for transportation of oil and gas which are usually assembled by the use of girth welds. Since flaws may naturally exist at such welds, fracture assessment of girth welded offshore pipelines is substantial. Current fracture assessment procedures like BS 7910 consider identical material properties for the weld and the base metals. However the strength dif...
متن کاملEffect of Heat Input of Submerged Arc Welding Process on the Corrosion Behavior of API X42 Gas Pipeline Steel Weld Joint
The effect of heat input of submerged arc welding process on the corrosion bahavior of weld metal of API X42 gas pipeline steel weld joint was investigated. For this purpose, 6 annealed sheets of 15mm thickness were prepared from the X42 microalloyed steel. Submerged arc welding process with varying heat input of 37.8, 18.9 and 12.6 kJ/mm was used for joint welding. Then potentiodynamic polariz...
متن کاملEffect of Heat Input of Submerged Arc Welding Process on the Corrosion Behavior of API X42 Gas Pipeline Steel Weld Joint
The effect of heat input of submerged arc welding process on the corrosion bahavior of weld metal of API X42 gas pipeline steel weld joint was investigated. For this purpose, 6 annealed sheets of 15mm thickness were prepared from the X42 microalloyed steel. Submerged arc welding process with varying heat input of 37.8, 18.9 and 12.6 kJ/mm was used for joint welding. Then potentiodynamic polariz...
متن کامل