Highly Transparent and UV-Resistant Superhydrophobic SiO2-Coated ZnO Nanorod Arrays
نویسندگان
چکیده
Highly transparent and UV-resistant superhydrophobic arrays of SiO2-coated ZnO nanorods are prepared in a sequence of low-temperature (<150 °C) steps on both glass and thin sheets of PET (2 × 2 in.(2)), and the superhydrophobic nanocomposite is shown to have minimal impact on solar cell device performance under AM1.5G illumination. Flexible plastics can serve as front cell and backing materials in the manufacture of flexible displays and solar cells.
منابع مشابه
UV-induced Wettability Change of Teflon-modified ZnO Nanorod Arrays on LiNbO3 Substrate
Aligned ZnO nanorod arrays films were grown on LiNbO3 substrates by aqueous growth, and subsequently rendered superhydrophobic with RF sputtered coated Teflon. The as-prepared surface exhibits superhydrophobicity with a water contact angle (CA) of 154.5. After 2 hours of UV irradiation on the surface, the surface wettability was approaching hydrophilic state; CA was measured to be 113. This stu...
متن کاملZnO nanorod array-coated mesh film for the separation of water and oil
Dense and vertically aligned ZnO nanorod arrays with a large area have been fabricated successfully on the stainless steel mesh by a simple chemical vapor deposition method. The coated mesh exhibited both superoleophilic and superhydrophobic properties, even if it was not modified by low surface energy materials. The separation efficiencies were more than 97% in the filtration of water and oil....
متن کاملFast UV detection by Cu-doped ZnO nanorod arrays chemically deposited on PET substrate
Well-aligned Cu-doped ZnO nanorods were successfully synthesized on polyethylene terephthalate (PET) substrate using chemical bath deposition method. The structural and optical properties of Cu-doped ZnO nanorods were investigated using X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), energy dispersive X-ray spectroscopy (EDX) and photoluminescence (PL) spectroscopy...
متن کاملInvestigating structural, optical and photocatalytic properties of hydrothermally synthesized ZnO nanorod arrays with various aspect ratios
ZnO nanorods with various aspect ratios (by changing the time of growth between 0-240 min) were synthesized using hydrothermal method and were investigated using XRD, SEM, UV–Vis and PL. It was found that growth time is directly coupled with the length, orientation and aspect ratio of the nanorod arrays. The optical transmittance of the NR arrays indicated a regular decrement of average transmi...
متن کاملGrowth and optical properties of ZnO nanorod arrays on Al-doped ZnO transparent conductive film
ZnO nanorod arrays (NRAs) on transparent conductive oxide (TCO) films have been grown by a solution-free, catalyst-free, vapor-phase synthesis method at 600°C. TCO films, Al-doped ZnO films, were deposited on quartz substrates by magnetron sputtering. In order to study the effect of the growth duration on the morphological and optical properties of NRAs, the growth duration was changed from 3 t...
متن کامل