Estimation of fatigue exposure from magnetic coercivity
نویسندگان
چکیده
An investigation of the effects of fatigue on A533B steel under constant load amplitude is reported in this paper. It was found that the plastic strain of the sample accumulated logarithmically with the number of stress cycles after initial fatigue softening. Based on the fact that plastic strain is often linearly related to the coercivity of material, at least for small changes of H c , a phenomenological relationship has been developed and tested to correlate the number of stress cycles to this magnetic parameter. This result represents the first successful attempt to relate the fatigue exposure directly to a magnetic parameter.
منابع مشابه
Magnetic Properties of Ni0.3Fe0.7 Alloy Nanowires
The effect of length variation on the magnetic properties of NiFe alloy nanowires electrodeposited into the alumina template was investigated. The diameter (45±2.5 nm) and length (~ 1.9, 7.12, 8.3, 9.5 and 13.3 µm) of the nanowires were estimated from scanning electron microscopy images. Energy dispersive spectroscopy results showed Ni3Fe7 composition of the alloy nanowire...
متن کاملخواص مغناطیسی نانو ذرات FeCo برای ذخیره سازی اطلاعات
Submicron FeCo magnetic grains with different percents of cobalt were grown in the presence of magnetic field. After omitting the excess ions and oxygen, heat treatment was performed and some samples were oriented in a polymer background in the presence of a magnetic field. The results of SEM, XRD, and magnetic measurements confirm the existence of induced magnetic anisotropy. As the strength...
متن کاملMicrowave-Assisted Synthesis of CuFe2O4 Nanoparticles and Starch-Based Magnetic Nanocomposites
Magnetic CuFe2O4 nanoparticles were synthesized by a facile microwave-assisted reaction between Cu(NO3)2 and Fe(NO3)3. The magnetic nanoparticles were added to starch to make magnetic polymeric nanocomposite. The nanoparticles and nanocomposites were characterized using X-ray diffraction and scanning electron microscopy. The magn...
متن کاملTHE EFFECT OF DY- DOPING ON THE STRUCTURAL AND MAGNETIC PROPERTIES OF MN-ZN FERRITE NANOPARTICLES
Mn0.8Zn0.2Fe2-xDyxO4 (where x= 0, 0.025, 0.05, 0.075, 0.1) ferrite nanoparticles were synthesized by auto- combustion sol-gel method for the first time in this study. The effect of Dy-doping on the structural and magnetic properties of the produced specimens was examined using the X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), vibrating sample magnetometery (VSM), and ...
متن کاملDoes Exposure to Static Magnetic Fields Generated by Magnetic Resonance Imaging Scanners Raise Safety Problems for Personnel?
MRI workers are occupationally exposed to static and time-varying gradient magnetic fields. While the 24-hour time-averaged exposure to static magnetic fields is about a few mT, the maximum static field strength can be as high as 500 mT during patient setup. Over the past several years, our laboratory has performed extensive experiments on the health effects of exposure of animal models and h...
متن کامل