Ultralow nanoscale wear through atom-by-atom attrition in silicon-containing diamond-like carbon.
نویسندگان
چکیده
Understanding friction and wear at the nanoscale is important for many applications that involve nanoscale components sliding on a surface, such as nanolithography, nanometrology and nanomanufacturing. Defects, cracks and other phenomena that influence material strength and wear at macroscopic scales are less important at the nanoscale, which is why nanowires can, for example, show higher strengths than bulk samples. The contact area between the materials must also be described differently at the nanoscale. Diamond-like carbon is routinely used as a surface coating in applications that require low friction and wear because it is resistant to wear at the macroscale, but there has been considerable debate about the wear mechanisms of diamond-like carbon at the nanoscale because it is difficult to fabricate diamond-like carbon structures with nanoscale fidelity. Here, we demonstrate the batch fabrication of ultrasharp diamond-like carbon tips that contain significant amounts of silicon on silicon microcantilevers for use in atomic force microscopy. This material is known to possess low friction in humid conditions, and we find that, at the nanoscale, it is three orders of magnitude more wear-resistant than silicon under ambient conditions. A wear rate of one atom per micrometre of sliding on SiO(2) is demonstrated. We find that the classical wear law of Archard does not hold at the nanoscale; instead, atom-by-atom attrition dominates the wear mechanisms at these length scales. We estimate that the effective energy barrier for the removal of a single atom is approximately 1 eV, with an effective activation volume of approximately 1 x 10(-28) m.
منابع مشابه
Nanoscale wear as a stress-assisted chemical reaction.
Wear of sliding contacts leads to energy dissipation and device failure, resulting in massive economic and environmental costs. Typically, wear phenomena are described empirically, because physical and chemical interactions at sliding interfaces are not fully understood at any length scale. Fundamental insights from individual nanoscale contacts are crucial for understanding wear at larger leng...
متن کاملMethod for characterizing nanoscale wear of atomic force microscope tips.
Atomic force microscopy (AFM) is a powerful tool for studying tribology (adhesion, friction, and lubrication) at the nanoscale and is emerging as a critical tool for nanomanufacturing. However, nanoscale wear is a key limitation of conventional AFM probes that are made of silicon and silicon nitride (SiNx). Here we present a method for systematically quantifying tip wear, which consists of sequ...
متن کاملMechanics of interaction and atomic-scale wear of amplitude modulation atomic force microscopy probes.
Wear is one of the main factors that hinders the performance of probes for atomic force microscopy (AFM), including for the widely used amplitude modulation (AM-AFM) mode. Unfortunately, a comprehensive scientific understanding of nanoscale wear is lacking. We have developed a protocol for conducting consistent and quantitative AM-AFM wear experiments. The protocol involves controlling the tip-...
متن کاملAssessment of the mechanical integrity of silicon and diamond-like carbon coated silicon atomic force microscope probes
The wear of atomic force microscope (AFM) tips is a critical issue in the performance of probe-based metrology and nanomanufacturing processes. In this work, diamond-like carbon (DLC) was coated on Si AFM tips using a plasma ion implantation and deposition process. The mechanical integrity of these DLC-coated tips was compared to that of uncoated silicon tips through systematic nanoscale wear t...
متن کاملSmall Amplitude Reciprocating Wear Performance of Diamond-like Carbon Films: Dependence of Film Composition and Counterface Material
Small amplitude (50 μm) reciprocating wear of hydrogen-containing diamond-like carbon (DLC) films of different compositions has been examined against silicon nitride and polymethyl-methacrylate (PMMA) counter-surfaces, and compared with the performance of an uncoated steel substrate. Three films were studied: a DLC film of conventional composition, a fluorine-containing DLC film (F-DLC), and si...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Nature nanotechnology
دوره 5 3 شماره
صفحات -
تاریخ انتشار 2010