Determination of Fretting Fatigue Behavior in Titanium Alloy Ti-6Al-4V: A review
نویسندگان
چکیده
5 Abstract-Fretting fatigue is an important concern in the structures and machine parts that are subjected to repeated relative movements between them. In current study a review of the work done by various researchers related to the evaluation of fretting fatigue response of Ti-6Al-4V has been presented. Effects of surface treatments, crack growth, heat treatments, types of loading, contact pad configuration on the fretting fatigue life have been presented. Life prediction models developed by various researchers have also been discussed.
منابع مشابه
An Experimental Investigation of Fretting Fatigue in Ti-6Al-4V: the Role of Contact Conditions and Microstructure
A systematic investigation of the fretting fatigue behavior of the titanium alloy Ti-6Al-4V in both the mill-annealed (MA) and the solution-treated and overaged (STOA) conditions was carried out. A sphere-on-flat fretting fatigue device was used that facilitated real-time control and monitoring of all the relevant parameters such as the contact geometry, contact (normal and tangential) loads, a...
متن کاملEffect of the Ultrasonic Surface Rolling Process on the Fretting Fatigue Behavior of Ti-6Al-4V Alloy
The effect of the ultrasonic surface rolling process (USRP) on the rotary bending fretting fatigue (FF) of Ti-6Al-4V alloy was investigated. The reason for the USRP's ability to improve the FF resistance of Ti-6Al-4V alloy was studied. The results revealed that the USRP induced a compressive residual stress field with a depth of 530 μm and a maximum residual stress of -930 MPa. Moreover, the su...
متن کاملFatigue and corrosion fatigue properties of Ti-6Al-4V implant grade titanium alloy in Ringer solution
Nowadays modification of metallic biomaterials which are used as implants for bone and hard tissues replacement is considered as an important subject. In the current study, corrosion fatigue properties of Ti-6Al-4V alloy investigated via Rotating-Bending standard test method and then, the results compared with the fatigue properties of the specimens tested in the same conditions. Scanning elect...
متن کاملInvestigation of the effect of temperature on the corrosion behavior of welded joints similar of titanium alloy Ti-6Al-4V by friction stir welding method
In this study, corrosion behavior of Ti-6Al-4V titanium alloy joint by friction stir welding with a rotational speed of 375 rpm and a travel speed of 100 mm/min was investigated. The welding procedure was carried out under β-transus temperature that was consisted of equiaxed grains in the stir zone. The corrosion behavior of the welded joint was investigated in 3.5% NaCl solution at temperature...
متن کاملEFFECTS OF TENSILE STRENGTH ON FATIGUE BEHAVIOR AND NOTCH SENSITIVITY OF TI-6AL-4V
In this research, rotating bending fatigue test at minimum to maximum stress ratio of R=-1 was used for investigating the fatigue behavior of Ti-6Al-4V alloy. Both smooth and notched specimens, with elastic concentration factor, kt, of approximately 3.6 and 4.1 were used for this purpose.In addition, the effect of variation in ultimate tensile strength, UTS, on the fatigue behavior of this allo...