Preparation and Preliminary Dialysis Performance Research of Polyvinylidene Fluoride Hollow Fiber Membranes
نویسندگان
چکیده
In this study, the separation properties of Polyvinylidene fluoride (PVDF) hollow fiber hemodialysis membranes were improved by optimizing membrane morphology and structure. The results showed that the PVDF membrane had better mechanical and separation properties than Fresenius Polysulfone High-Flux (F60S) membrane. The PVDF membrane tensile stress at break, tensile elongation and bursting pressure were 11.3 MPa, 395% and 0.625 MPa, respectively. Ultrafiltration (UF) flux of pure water reached 108.2 L∙h-1∙m-2 and rejection of Albumin from bovine serum was 82.3%. The PVDF dialyzers were prepared by centrifugal casting. The influences of membrane area and simulate fluid flow rate on dialysis performance were investigated. The results showed that the clearance rate of urea and Lysozyme (LZM) were improved with increasing membrane area and fluid flow rate while the rejection of albumin from bovine serum (BSA) had little influence. The high-flux PVDF dialyzer UF coefficient reached 62.6 mL/h/mmHg. The PVDF dialyzer with membrane area 0.69 m2 has the highest clearance rate to LZM and urea. The clearance rate of LZM was 66.8% and urea was 87.7%.
منابع مشابه
Preparation of Polyvinylidene Fluoride (PVDF) Hollow Fiber Hemodialysis Membranes
In this study, the polyvinylidene fluoride (PVDF) hollow fiber hemodialysis membranes were prepared by non-solvent induced phase separation (NIPS). The influences of PVDF membrane thickness and polyethylene glycol (PEG) content on membrane morphologies, pore size, mechanical and permeable performance were investigated. It was found that membrane thickness and PEG content affected both the struc...
متن کاملPolyvinylidene Fluoride Hollow Fiber Membrane Contactor Incorporating Surface Modifying Macromolecule for Carbon Dioxide Stripping from Water
Porous surface modified polyvinylidene ïuoride (PVDF) hollow fiber membranes are fabricated through a dry-wet phased inversion process. Surface modifying macromolecules (SMM) (1 wt. %) are used as additives in the spinning dope. The performance of the surface modified membrane in contactor application for CO2 stripping from water is assessed through the fabricated gas–liquid membrane contacto...
متن کاملCorrelated Effect of Air Gap and PVP Concentration on the Structure and Performance of PVDF Ultrafiltration Hollow Fiber Membrane
Polyvinylidene fluoride/polyvinylpyrrolidone (PVDF/PVP) hollow fiber membranes were fabricated by dry-jet wet-spinning process. The correlated effects of the air gap length and PVP concentration ((1) the air gap length effect at the low and high PVP concentration in the dope solutions, as well as (2) the effect of the PVP concentration at the same air gap length) on the cross-section structure ...
متن کاملCorrelated Effect of Air Gap and PVP Concentration on the Structure and Performance of PVDF Ultrafiltration Hollow Fiber Membrane
• The air gap effect on PVDF hollow fiber membranes is much more evident for the dope solution with the high PVP concentration than low PVP concentration. • Large macro-voids/cavities in PVDF hollow fiber membranes are suppressed to the finger-like macro-voids and the separation layer is thickened when increasing PVP concentration in dope solution. • The hydrophilicity and viscosity of polymer ...
متن کاملMunicipal Wastewater Treatment Using a Hollow Fiber Membrane Bioreactor
A bioreactor equipped with hollow fiber microfiltration membranes was applied for wastewater treatment. Removal of chemical oxygen demand (COD) and biochemical oxygen demand (BOD5) was investigated. The experimental setup consisted of influent and effluent tanks, and membrane modules using Polyvinyl Di–Fluoride (PVDF) hollow fibers. The operation program included suction and backwash...