Heteroepitaxial diamond growth on 4H-SiC using microwave plasma chemical vapor deposition
نویسندگان
چکیده
Deposition of heteroepitaxial diamond via microwave chemical vapor deposition has been performed on a 4H-SiC substrate using bias enhanced nucleation followed by a growth step. In future work, the diamond film will serve as a protective layer for an alpha particle sensor designed to function in an electrorefiner during pyroprocessing of spent fuel. The diamond deposition on the 4H-SiC substrate was carried out using a methane-hydrogen gas mixture with varying gas flow rates. The nucleation step was conducted for 30 minutes and provided sufficient nucleation sites to grow a diamond film on various locations on the substrate. The resulting diamond film was characterized using Raman spectroscopy exhibiting the strong Raman peak at 1332 cm-1. Scanning electron microscopy was used to observe the surface morphology and the average grain size of the diamond film was observed to be on the order of ∼2-3 μm.
منابع مشابه
Carbon nanotube array thermal interfaces for high-temperature silicon carbide devices
Multiwalled carbon nanotube (MWCNT) arrays have been directly synthesized from templated Fe2O3 nanoparticles on the C-face of 4H-SiC substrates by microwave plasma chemical vapor deposition (MPCVD), and the room-temperature thermal resistances of SiC-MWCNT-Ag interfaces at 69–345 kPa as well as the thermal resistances of SiCMWCNT-Ag interfaces up to 250 C (at 69 kPa) have been measured using a ...
متن کاملMicrowave plasma chemical vapour deposition diamond nucleation on ferrous substrates with Ti and Cr interlayers
Diamond-coated steel is considered an important issue in synthetic diamond technology due to the great economical importance of enhancing the wear resistance and surface hardness of commercial Fe-based alloys. However, direct diamond coating by chemical vapour deposition (CVD) is rather problematic—adhesion and growth are seriously affected. The use of interlayers is a common approach to minimi...
متن کاملEllipsometric investigation of nitrogen doped diamond thin films grown in microwave CH4/H2/N2 plasma enhanced chemical vapor deposition
متن کامل
Understanding the chemical vapor deposition of diamond: recent progress.
In this paper we review and provide an overview to the understanding of the chemical vapor deposition (CVD) of diamond materials with a particular focus on the commonly used microwave plasma-activated chemical vapor deposition (MPCVD). The major topics covered are experimental measurements in situ to diamond CVD reactors, and MPCVD in particular, coupled with models of the gas phase chemical an...
متن کاملDielectric properties of hydrogen-incorporated chemical vapor deposited diamond thin films
Diamond thin films with a broad range of microstructures from a ultrananocrystalline diamond (UNCD) form developed at Argonne National Laboratory to a microcrystalline diamond (MCD) form have been grown with different hydrogen percentages in the Ar/CH4 gas mixture used in the microwave plasma enhanced chemical vapor deposition (CVD) process. The dielectric properties of the CVD diamond thin fil...
متن کامل