Effect of degradation of denture base resin on bond strength to relining resins.
نویسندگان
چکیده
The purpose of this study was to evaluate the effect of degradation of a denture base resin on bond strength to relining resins. Denture base resin specimens were immersed under various conditions to simulate degradation. Tensile bond strength of denture base resin after immersion to relining resins was measured with or without surface grinding. The bond strength of denture base resin without grinding after immersion to relining resin was significantly lower than that before immersion. However, bond strength was improved by surface grinding before bonding. These results suggest that bonding efficiency of denture base resin to relining resins was affected by immersion condition, which caused potential degradation of the denture base resin.
منابع مشابه
Evaluation of adhesion of reline resins to the thermoplastic denture base resin for non-metal clasp denture.
This study aimed to evaluate the tensile and transverse bond strength of chairside reline resins (Tokuyama Rebase II, Mild Rebaron LC) to a thermoplastic acrylic resin (Acrytone) used for non metal clasp denture. The results were compared with those of a conventional heat polymerized acrylic resin (Paladent 20) and a thermoplastic polyamide resin (Biotone). The failure sites were examined by sc...
متن کاملFactors affecting the bond strength of denture base and reline acrylic resins to base metal materials
OBJECTIVE The shear bond strengths of two hard chairside reline resin materials and an auto-polymerizing denture base resin material to cast Ti and a Co-Cr alloy treated using four conditioning methods were investigated. MATERIAL AND METHODS Disk specimens (diameter 10 mm and thickness 2.5 mm) were cast from pure Ti and Co-Cr alloy. The specimens were wet-ground to a final surface finish of 6...
متن کاملShear Bond Strength of Acrylic Denture Teeth to PMMA and Polyamide Denture Base Materials
Introduction: Detachment of denture teeth from denture base is one of the most common reasons for costly denture repairs .This study aimed at evaluating the bond strength of an acrylic denture tooth to polyamide injection-molded thermoplastic denture base material compared with three conventional polymethylmethacrylate (PMMA) denture base resins. Materials and Method: A total of 40 acrylic dent...
متن کاملIn-vitro study of the fracture resistance of denture base resin with resilient reline material
Purpose: This study aimed to analyze the fracture resistance of denture base resins relined with either a conventional rigid resin or a new resilient resin. Materials and Methods: Two types of test plates were fabricated by relining the base resin (Acron) with a conventional rigid resin (Tokuso Rebase, TR) or a newly developed relining resin (Tokuyama Rebase II, RII). The specimens were divided...
متن کاملBond Strength of Hard Chairside Reline Resins to a Rapid Polymerizing Denture Base Resin before and after Thermal Cycling
PURPOSE This study assessed the shear bond strength of 4 hard chairside reline resins (Kooliner, Tokuso Rebase Fast, Duraliner II, Ufi Gel Hard) to a rapid polymerizing denture base resin (QC-20) processed using 2 polymerization cycles (A or B), before and after thermal cycling. MATERIALS AND METHODS Cylinders (3.5 mm x 5.0 mm) of the reline resins were bonded to cylinders of QC-20 polymerize...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Dental materials journal
دوره 26 1 شماره
صفحات -
تاریخ انتشار 2007