Preparation and Characterization of Tetracomponent ZnO/SiO2/SnO2/TiO2 Composite Nanofibers by Electrospinning

نویسندگان

  • Chao Song
  • Xiangting Dong
چکیده

[Zn(CH3COO)2 + PVP]/[C2H5O)4Si + PVP]/[SnCl4 + PVP]/[Ti(OC4H9)4 + CH3COOH + PVP] precursor composite fibers have been fabricated through self-made electrospinning equipment via electrospinning technique. ZnO/SiO2/ SnO2/TiO2 composite nanofibers were obtained by calcination of the relevant precursor composite fibers. The samples were characterized by thermogravimetric-differential thermal analysis (TG-DTA), X-ray diffractometry (XRD), Fourier transform infrared spectroscopy (FTIR), and Scanning electron microscopy (SEM). TG-DTA analysis reveals that solvents, organic compounds and inorganic in the precursor composite fibers are decomposed and volatilized totally, and the mass of the samples kept constant when sintering temperature was above 900 ̊C, and the total mass loss percentage is 88%. XRD results show that the precursor composite fibers are amorphous in structure, and pure phase ZnO/SiO2/ SnO2/TiO2 composite nanofibers are obtained by calcination of the relevant precursor composite fibers. FTIR analysis manifests that pure inorganic oxides are formed. SEM analysis indicates that the width of the precursor composite fibers is ca. 1.485 ± 0.043 μm. The width of the ZnO/SiO2/SnO2/TiO2 composite nanofibers is ca. 1145.098 ± 68.093 nm.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Synthesis of Polypyrrole Coated SnO2-ZnO Electrospun Nanofibers via Vapor Phase Polymerization Method

This paper reports the synthesis of polypyrrole coated SnO2/ZnOelectrospunnanofibers via vapor phase polymerization method. In order to prepare one dimensional (SnO2- ZnO)/polypyrrole with the core sheath structure, first SnO2-ZnO composite nanofibers were synthesized via electrospinning method followed by adsorption of Fe 3+  on the surface of the SnO2-ZnO nanofibers and finally pyrrole w...

متن کامل

Nanocomposite ZnO–SnO2 Nanofibers Synthesized by Electrospinning Method

We report the characterization of mixed oxides nanocomposite nanofibers of (1 - x) ZnO-(x)SnO2 (x ≤ 0.45) synthesized by electrospinning technique. The diameter of calcined nanofibers depends on Sn content. Other phases like SnO, ZnSnO3, and Zn2SnO4 were absent. Photoluminescence studies show that there is a change in the blue/violet luminescence confirming the presence of Sn in Zn-rich composi...

متن کامل

Electrospun ZnO/TiO2 composite nanofibers as a bactericidal agent.

Novel ZnO/TiO(2) composite nanofibers were fabricated by an electrospinning method and showed excellent antimicrobial activity against gram-negative Escherichia coli and gram-positive Staphylococcus aureus under UV irradiation and in the absence of light.

متن کامل

Preparation and Characterization of SnO2 Nanofibers via Electrospinning

Tin oxide (SnO2) nanofibers are successfully prepared by electrospinning homogeneous viscous solutions of tin acetate in polyvinylpyrrolidone (PVP). The electrospinning is carried out by applying a DC voltage to the tip of a syringe and maintaining the tip to collector distance (TCD), i.e. at DC electric field of 1.25 kV∙cm−1. The electrospun nanofibers are calcined between 550 ̊C and 650 ̊C for ...

متن کامل

Preparation of PVDF/SiO2 Composite Nanofiber Membrane Using Electrospinning for Polymer Electrolyte Analysis

Superhydrophobic poly(vinylidene fluoride) PVDF-SiO2 composite membranes with different % of SiO2 contents were prepared by electrospinning. The surface morphologies of the membranes are characterized by using scanning electron microscopy. The nanofibers in the membranes were stacked in layers to produce fully interconnected pores that resulted in high porosity. The incorporation of SiO2 into t...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2013