Gamma-radiolysis-assisted cobalt oxide nanoparticle formation.

نویسندگان

  • L M Alrehaily
  • J M Joseph
  • M C Biesinger
  • D A Guzonas
  • J C Wren
چکیده

The formation of Co(3)O(4) nano-scale colloid particles by gamma irradiation of CoSO(4) solutions was investigated. Solutions of 0.2-0.3 mM CoSO(4) at pH 6.0 and 10.6 (air-saturated and Ar-purged) were irradiated at an absorbed dose rate of 5.5 kGy h(-1). The resulting concentrations of H(2), H(2)O(2), Co(II) and Co(III) species in solution and the chemical composition and sizes of particles that were formed were measured as a function of irradiation time. Particle formation was observed only for initially air-saturated CoSO(4) solutions at pH 10.6. Analysis of the particle formation as a function of irradiation time shows that the particles evolve from Co(OH)(2) to CoOOH and then to Co(3)O(4). The radiolytic oxidation of Co(II) to Co(III) was completed in 100 min and the chemical composition of the final particles was identified as Co(3)O(4) by XPS, Raman and UV-Vis spectroscopy. Transmission electron microscopy (TEM) images show the final particles are approximately uniform in size, ranging from 8 to 20 nm. A mechanism is proposed to explain the particle formation. A key factor is the low solubility of Co(OH)(2) in air-saturated solutions at high pH. This mechanism for particle formation is compared with the mechanism previously reported for the radiolytic formation of γ-FeOOH nanoparticles.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Water radiolysis by gamma –irradiation for high quality synthesis of Nickel Oxide nano sheet

A simple, time effective and cost effective, methos was reported for synthesis of nickel oxide nanostructure. The NiO nanostructure was synthesized by gamma-irradiation method from NiSO4 precursor. The solution was irradiated by 60Co gamma-ray source at the dose rate of 40 Gy/min for determined time. The synthesized powders are characterized by means of X-ray powder diffraction (XRD), Energy-di...

متن کامل

A comparative study of gamma, electron beam, and synchrotron X-ray irradiation method for synthesis of silver nanoparticles in PVP

A one-pot synthesis method has been developed for preparation of silver nanoparticles in aqueous poly (vinyl pyrrolidone) (PVP) solution by synchrotron X-ray radiation. The hydrated electrons (eaqˉ) and hydrogen atom radical (H·), products of radiolysis of water molecules by synchrotron X-rays brings about the reduction of the metal ions, resulting in homogeneous nucleation and nanoparticle for...

متن کامل

Metal-organic frameworks of cobalt and nickel centers with carboxylate and pyridine functionality linkers: Thermal and physical properties; precursors for metal oxide nanoparticle preparation

This  article  provides  an  overview  on  preparation,  design,  crystal structure  and  properties  of  some  metal-organic  frameworks  of carboxylate coordination polymers mixed with pyridine-functionality linkers  prepared  in  our  laboratory.  The  article  covers  coordination polymers  in  two-  and  three-dimensional  supramolecular architectures. The reported coordination polyme...

متن کامل

Edge reactivity and water-assisted dissociation on cobalt oxide nanoislands

Transition metal oxides show great promise as Earth-abundant catalysts for the oxygen evolution reaction in electrochemical water splitting. However, progress in the development of highly active oxide nanostructures is hampered by a lack of knowledge of the location and nature of the active sites. Here we show, through atom-resolved scanning tunnelling microscopy, X-ray spectroscopy and computa...

متن کامل

Colloidal polymerization of polymer-coated ferromagnetic nanoparticles into cobalt oxide nanowires.

The preparation of polystyrene-coated cobalt oxide nanowires is reported via the colloidal polymerization of polymer-coated ferromagnetic cobalt nanoparticles (PS-CoNPs). Using a combination of dipolar nanoparticle assembly and a solution oxidation of preorganized metallic colloids, interconnected nanoparticles of cobalt oxide spanning micrometers in length were prepared. The colloidal polymeri...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Physical chemistry chemical physics : PCCP

دوره 15 3  شماره 

صفحات  -

تاریخ انتشار 2013