Thin films sputtered from Ba2NdFeNb4O15 multiferroic targets on BaFe12O19 coated substrates

نویسندگان

  • Romain Bodeux
  • Dominique Michau
  • Mario Maglione
  • Michaël Josse
چکیده

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Enhanced Physical Properties Of Indium Tin Oxide Films Grown on Zinc Oxide-Coated Substrates

Structural, electrical and optical properties of indium tin oxide or ITO (In2O3:SnO2) thin films on different substrates are investigated. A 100-nm-thick pre-deposited zinc oxide (ZnO) buffer layer is utilized to simultaneously improve the electrical and optical properties of ITO films. High purity ZnO and ITO layers are deposited with a radio frequency sputtering in argon ambient with plasma p...

متن کامل

Studies on sol-gel dip-coated nanostructured ZnO thin films

Nanostructured ZnO thin films were prepared by sol-gel dip coating technique. Zinc acetate and ammonium hydroxide were used as precursors and ethanol was as solvent. Ammonium hydroxide (NH4OH) solution was added drop-wise under vigorous stirring to obtain the sol-gel of different pH (varying from 6.9 to 7.2). ZnO thin films were obtained by dipping the glass substrates for few seconds and then ...

متن کامل

Optical properties of spin-coated Er-doped Ga1As39S60 Chalcogenide thin films

Spin-coating of Chalcogenide glasses is a cost-effective and flexible method to produce thin films applicable in photonics. In this paper Er was doped into Ga1As39S60 glass by melt quenching technique and solutions for spin coating were prepared from glass powders dissolved in Propylamine and Ethylendiamine. Substrates used were microscopic slides (refractive index of about 1.51). Applied layer...

متن کامل

Residual Stress in Cu Sputtered Films on Glass Substrates at Different Substrate Temperatures

Copper films of 300 nm thickness deposited by planar magnetron sputtering on glass substrates, for substrate temperatures between 300 and 500 K, and deposition rate of 10 ?s?1. Microstructure of these films was obtained by X-ray diffraction, while the texture mode of diffractometer was used for stress measurement by the sin2? technique. The components of the stress tensor are obtained using mea...

متن کامل

Effect of Substrate Bias Voltage and Ti Doping on the Tribological Properties of DC Magnetron Sputtered MoSx Coatings‌

Molybdenum disulfide (MoS2) is one of the most widely used solid lubricants. In this work, composite MoSx/Ti coatings were deposited by direct-current magnetron sputter ion plating onto plain carbon steel substrates. The MoSx/Ti ratio in the coatings was controlled by sputtering the composite targets. The composition, microstructure, and mechanical properties of the coatings were explored using...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2017