Effect of additives on the compressive strength and setting time of a Portland cement.
نویسندگان
چکیده
Improvements in strength and setting time of Portland cements (PC) are needed to enhance their performance as endodontic and load bearing materials. This study sought to enhance the compressive strength and setting time of a PC by adding one of the following additives: 20% and 30% poly-methylmethacrylate (PMMA), 20% and 30% irregular and spherical amalgam alloys, and 10% CaCl(2). The control consisted of unreinforced PC specimens. Setting time was determined using a Gillmore apparatus according to standardized methods while compressive strength was measured using a universal testing machine after 21 hours or 60 days of water storage. Data were analyzed by ANOVA, Tukey and Games-Howell tests (alpha = 5%). All additives significantly decreased both initial and final setting times as compared with the PC-control (p < .05). 30% PMMA and 30% irregular alloy had the lowest values of initial setting time. 30% irregular alloy also produced the lowest values of final setting time while 30% spherical alloy yielded the highest (p < .05). No differences were detected between the compressive strength values of 21 hours and 60 days. While 10% CaCl(2), 20% and 30% PMMA produced values significantly lower than the PC-control, 30% spherical alloy significantly improved the compressive strength of the reinforced PC (p < .05). In summary, all additives significantly reduced the setting time and 30% spherical amalgam alloy yielded a significant increase in compressive strength for the tested PC, which might represent an improved composition for PCs to expand their use as endodontic and potentially load bearing materials.
منابع مشابه
Solidification/Stabilization of Lead Contaminated Soil Using Magnesia Phosphate cement and Ordinary Portland cement
Background and objectives: Solidification/stabilization is an effective technique for reducing the leachability of contaminants in soils. Magnesia phosphate cement and ordinary Portland cement can be used to remediate soils contaminated. In this study, the performance of the solidified/stabilized soil was compared for mixtures composed of magnesia phosphate and ordinary Portland cement. Materia...
متن کاملComparative Study of the Physical Properties of Some Brands of Portland Cement Available in the Libyan Market
The quality of cement is one of the important factors which materially contribute to the strength and durability of structural concrete. Different brands of Portland cement are used in Libya by local contractors for various construction work. However, no comparative study has been made undertaken hitherto to investigate the mechanical and physical properties of the various brands of cement. Thi...
متن کاملINVESTIGATING THE LINEAR EXPANSION, SET, AND STRENGTH BEHAVIORS OF THE BINARY MIXTURE PORTLAND CEMENT CLINKER-GYPSUM
Abstract: The linear expansion, early-age compressive strength and setting times of the binary mixtures of gypsum and Portland cement clinkers of relatively low C3A-contents were investigated. For this reason, type 1, 2, and 5 of Portland cement-clinkers were selected and a number of binary mixtures were designed. At relatively lower percentages of gypsum (about 5%), the early strength behavior...
متن کاملEffect of Use of Granulated Slag Instead of Portland Cement on the Properties of Concrete
In this research, 210 concrete cube specimens (15cm) were made replacing 0, 5, 10, 15, 20, 25, 30, 35, 40, 50, and 60 percent of slag powder from Isfahan Steel Mill for cement. The control specimens were made with 350 kg/m3 cement content and the water cement ratio in all specimens was 0.51. The Slump value and compressive strength of concrete specimens in 7, 28 and 90 days were obtained and th...
متن کاملEffect of Use of Granulated Slag Instead of Portland Cement on the Properties of Concrete
In this research, 210 concrete cube specimens (15cm) were made replacing 0, 5, 10, 15, 20, 25, 30, 35, 40, 50, and 60 percent of slag powder from Isfahan Steel Mill for cement. The control specimens were made with 350 kg/m3 cement content and the water cement ratio in all specimens was 0.51. The Slump value and compressive strength of concrete specimens in 7, 28 and 90 days were obtained and th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Brazilian oral research
دوره 24 2 شماره
صفحات -
تاریخ انتشار 2010