Synchrotron X-ray Microdiffraction Images of Polarization Switching in Epitaxial PZT Capacitors with Pt and SrRuO3 Top Electrodes

The evolution of stored ferroelectric polarization in PZT thin film capacitors was imaged using synchrotron x-ray microdiffraction with a submicron-diameter focused incident x-ray beam. To form the capacitors, an epitaxial Pb(Zr,Ti)O3 (PZT) thin film was deposited on an epitaxiallygrown conductive SrRuO3 (SRO) bottom electrode on a SrTiO3 (STO) (001) substrate. Polycrystalline SRO or Pt top electrodes were prepared by sputter deposition through a shadow mask and subsequent annealing. The intensity of x-ray reflections from the PZT film depended on the local ferroelectric polarization. With 10 keV x-rays, regions of opposite polarization differed in intensity by 26% in our PZT capacitor with an SRO top electrode. Devices with SRO electrodes showed just a 25% decrease in the remnant polarization after 10 switching cycles. In devices with Pt top electrodes, however, the switchable polarization decreased a by 70% after only 5×10 cycles.