ADSORPTION OF CONGO RED DYE ON HAZELNUT SHELLS AND DEGRADATION WITH Phanerochaete chrysosporium
نویسندگان
چکیده
The present work concerns the experimental evaluation of hazelnut shells as a low cost natural biosorbent. Adsorption of the direct azo dye Congo Red was performed within a concentrations range of 50-5000 mg/L. Hazelnut shells were employed as organic support for Phanerochaete chrysosporium cultures to study the best cultural medium composition for the MnP production. The capability of Phanerochaete chrysosporium to take macronutrients as carbon and nitrogen from hazelnut shells was demonstrated. Cultures of Phanerochaete chrysosporium were carried out with hazelnut shells coming from Congo Red adsorption tests, showing that 43% of the adsorbed dye was degraded.
منابع مشابه
Degradation of Phthalocyanine by a Core-Shell TiO2 Photocatalyst: Effect of Iron Dopping on Band Gap
In this research, initially, the sol-gel method was employed to produce γ-alumina and TiO2 catalysts with core-shell structure. Iron (III) was used as a dopant. The newlyproduced core-shells were Fe/TiO2// Fe/ γ-Al2O3 (FTFA). Sulfonated cobalt phthalocyanine was used as a dye pollutant in Merox process. By doping Fe in TiO2 catalyst, the ef...
متن کاملXAFS Study of Arsenical Nickel Hydroxide
To Investigate the role played by nickel co-ions in contributing to the stability of arsenic, fluorescence XAFS measurements at both arsenic K-edge and nickel K-edge, respectively, on amorphous arsenical nickel hydroxide, crystalline arsenical nickel hydroxide, and annabergite reference compounds have been carried out. The XAFS results indicate that the arsenic-bearing nickel hydroxides have a ...
متن کاملSynthesis of multi-shelled ZnO hollow microspheres and their improved photocatalytic activity
Herein, we report an effective, facile, and low-cost route for preparing ZnO hollow microspheres with a controlled number of shells composed of small ZnO nanoparticles. The formation mechanism of multiple-shelled structures was investigated in detail. The number of shells is manipulated by using different diameters of carbonaceous microspheres. The products were characterized by X-ray powder di...
متن کاملVisible-light photochemical activity of heterostructured core-shell materials composed of selected ternary titanates and ferrites coated by tiO2.
Heterostructured photocatalysts comprised of microcrystalline (mc-) cores and nanostructured (ns-) shells were prepared by the sol-gel method. The ability of titania-coated ATiO3 (A = Fe, Pb) and AFeO3 (A = Bi, La, Y) catalysts to degrade methylene blue in visible light (λ > 420 nm) was compared. The catalysts with the titanate cores had enhanced photocatalytic activities for methylene blue deg...
متن کاملVisible light photochemical activity of heterostructured PbTiO3–TiO2 core–shell particles
Heterostructured powders composed of microcrystalline PbTiO3 cores coated with nanostructured TiO2 shells were prepared by a sol–gel method. When exposed to visible light (l 4 420 nm), the heterostructured powder degrades methylene blue at a rate 4.8 times greater than PbTiO3, TiO2, or mechanical mixtures of the phases. The rate at which the heterostructured powder degrades methylene blue depen...
متن کامل