A ug 2 00 1 Magnetic relaxation and critical current density of MgB 2 thin films
نویسندگان
چکیده
Magnetic relaxation and critical current density have been measured on a M gB 2 thin film in a wide region of temperature with the magnetic field up to 8 T. The irreversibility line has also been determined. It is found that the relaxation rate has a very weak temperature dependence below 1/2T c showing a clear residual relaxation rate at zero K, which cannot be easily explained as due to thermally activated flux creep. Furthermore the relaxation rate has a strong field dependence. The flux dynamics of thin films are very similar to that of high pressure synthesized bulks although the relaxation rate in thin film is systematically higher than that of a bulk sample. All the results here together with those from the bulk samples suggest that the flux dynamics may be dominated by the quantum effects, such as quantum fluctuation and tunneling.
منابع مشابه
nd - m at . s up r - co n ] 1 9 A ug 2 00 1 Suppression of Superconducting Critical Current Density by Many Small Flux Jumps in MgB 2 Thin Films
By doing magnetization measurements during magnetic field sweeping on thin films of the new superconductor MgB2, it is found that in low temperature and low field region many small flux jumps are taking place. This effect strongly suppresses the central magnetization peak leading to an reduced nominal superconducting critical current density at low temperatures. A borderline for this effect to ...
متن کامل1 Suppression of Superconducting Critical Current Density by Small Flux Jumps in MgB 2 Thin Films
By doing magnetization measurements during magnetic field sweeps on thin films of the new superconductor MgB2, it is found that in a low temperature and low field region small flux jumps are taking place. This effect strongly suppresses the central magnetization peak leading to reduced nominal superconducting critical current density at low temperatures. A borderline for this effect to occur is...
متن کاملEnhancement of the critical current density in FeO-coated MgB2 thin films at high magnetic fields
The effect of depositing FeO nanoparticles with a diameter of 10 nm onto the surface of MgB(2) thin films on the critical current density was studied in comparison with the case of uncoated MgB(2) thin films. We calculated the superconducting critical current densities (J(c)) from the magnetization hysteresis (M-H) curves for both sets of samples and found that the J(c) value of FeO-coated film...
متن کاملar X iv : c on d - m at / 0 70 17 80 31 J an 2 00 7 Scaling of resistivities and guided vortex motion in MgB 2 thin films
Longitudinal and transverse voltages have been measured on thin films of MgB 2 with different superconducting transition widths. The study has been performed in zero and non-zero external magnetic fields. The non-zero transverse voltage has been observed in close vicinity of the critical temperature in zero external magnetic field, while further away from T c this voltage becomes zero. In magne...
متن کاملar X iv : c on d - m at / 0 30 44 78 22 A pr 2 00 3 Upper critical fields of MgB 2 thin films
Critical fields of four MgB 2 thin films with a normal state resistivity ranging from 5 to 50 µΩcm and T c from 29.5 to 38.8 K were measured up to 28 T. H c2 (T) curves present a linear behavior towards low temperatures. Very high critical field values have been found, up to 24 T along the c-axis and 57 T in the basal plane not depending on the normal state resistivity values. In this paper, cr...