Microstructures, Hardness and Corrosion Behaviors of FeCoNiNb0.5Mo0.5 and FeCoNiNb High-Entropy Alloys
نویسندگان
چکیده
This study investigates the effects of niobium and molybdenum on FeCoNi alloy, including on the microstructures and hardness of FeCoNiNb0.5Mo0.5 and FeCoNiNb alloys, and the polarization behaviors of these alloys in 1 M sulfuric acid and 1 M sodium chloride solutions. The results in this study indicate that both FeCoNiNb0.5Mo0.5 and FeCoNiNb alloys had a dual-phased dendritic microstructure; all of the phases in these alloys were solid solution phases, and no ordering was observed. Therefore, the solid solution effect significantly increased the hardness of these two alloys; in particular, FeCoNiNb alloy had the highest hardness of the alloys of interest. The corrosion resistance of FeCoNiNb0.5Mo0.5 and FeCoNiNb alloys was less than that of FeCoNi alloy because of their dual-phased dendritic microstructures. The corrosion resistance of the FeCoNiNb0.5Mo0.5 alloy exceeded that of the FeCoNiNb alloy in these solutions. However, FeCoNiNb0.5Mo0.5 and FeCoNiNb alloys exhibited a favorable combination of corrosion resistance and hardness.
منابع مشابه
Study of the Precipitation Hardening Behaviour and Intergranular Corrosion of Al-Mg-Si Alloys with Differing Si Contents
The effects of Si addition on the precipitation hardening behaviour and evolution of intergranular corrosion (IGC) of Al-Mg-Si alloys were investigated using hardness tests, scanning electron microscopy (SEM), potentiodynamic polarization measurements, and high-resolution transmission electron microscopy (HRTEM). With an increase of the Si content, the peak hardness of the Al-Mg-Si alloys consi...
متن کاملEffect of Creep Aging Process on Microstructures and Properties of the Retrogressed Al-Zn-Mg-Cu Alloy
The creep aging behaviors of retrogressed Al-Zn-Mg-Cu alloy were studied by uniaxial tensile creep tests at 140 ◦C. The effects of creep aging time and applied stress on microstructures and properties of the studied alloy were investigated by using transmission electron microscope (TEM), hardness, and corrosion resistance tests. Results show that the effects of the creep aging process on micros...
متن کاملTribological and corrosion behaviors of warm-and hot-rolled Ti-13Nb-13Zr alloys in simulated body fluid conditions
Development of submicrocrystalline structure in biomedical alloy such as Ti-13Nb-13Zr (in wt%) through warm-rolling process has been found to enhance mechanical properties compared to conventional thermomechanical processing routes including hot-rolling process. The present study investigated the tribological and corrosion behaviors of warm-rolled (WR) and hot-rolled Ti-13Nb-13Zr alloys which h...
متن کاملMicrostructures of Al7.5Cr22.5Fe35Mn20Ni15 High-Entropy Alloy and Its Polarization Behaviors in Sulfuric Acid, Nitric Acid and Hydrochloric Acid Solutions
This paper investigates the microstructures and the polarization behaviors of Al7.5Cr22.5Fe35Mn20Ni15 high-entropy alloy in 1M (1 mol/L) deaerated sulfuric acid (H2SO4), nitric acid (HNO3), and hydrochloric acid (HCl) solutions at temperatures of 30–60 ̋C. The three phases of the Al7.5Cr22.5Fe35Mn20Ni15 high-entropy alloy are body-centered cubic (BCC) dendrites, face-centered cubic (FCC) interd...
متن کاملDetecting pitting corrosion and its severity using wavelet entropy in electrochemical noise measurement
Entropy as a measure of uncertainty was used to represent the results of the wavelet technique in electrochemical noise analysis. The experimental signals were obtained by recording the electrochemical potential and current noise of 7075 aluminum alloy in 3.5% NaCl solution. The electrochemical potential and current noise were decomposed into 16 levels using Daubechies wavelets. Wavelet output ...
متن کامل