Leaching behaviour of a galvanic sludge in sulphuric acid and ammoniacal media.

نویسندگان

  • J E Silva
  • D Soares
  • A P Paiva
  • J A Labrincha
  • F Castro
چکیده

Leaching studies of a sludge produced by the physico-chemical treatment of wastewaters generated by a Ni/Cr plating plant were carried out in both sulphuric acid and ammoniacal media aiming to decide which of them would be the best treatment for this kind of waste material. The dissolution behaviour of some metals (Cu, Ni, Cr and Zn) was studied in order to assure the best metal recovery conditions in subsequent processes by the use of some separation methods such as solvent extraction and precipitation techniques. Therefore, the study here presented deals with the first chemical stage of an integrated treatment process. For the sulphuric acid leaching, maximal conversions obtained were 88.6% Cu, 98.0% Ni and 99.2% Zn for the following experimental conditions: a 100 g L(-1) acid concentration, a 5:1 liquid-to-solid ratio (L/S), a particle size less than 1 mm, a digestion time of 1h, a stirring speed of 700 rpm (all at room temperature and under atmospheric pressure). As expected, no selectivity was achieved for the sulphuric acid leaching, despite this option yielding much higher metal ion dissolution when compared with that reached by ammoniacal leaching. The use of this latter medium allowed the extraction of Cu and Ni without Cr species, but rates of conversion were only about 70% for Cu and 50% for Ni, much lower than those obtained for sulphuric acid leaching.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Leaching of basic oxygen furnace sludge with sulphuric acid

In this study the hydrometallurgical processing of BOF sludge in the sulphuric acid solutions under atmospheric pressure and temperatures up to 100 °C is investigated on a laboratory scale. The influence of sulphuric acid concentration, temperature, time and liquid to solid ratio (L:S) on the leaching process was studied. The main aim of this study was to determine optimal conditions when the m...

متن کامل

Kinetics of chalcopyrite galvanic leaching using sulfate media at the low temperature in the GalvanoxTM process

In this research work, the dissolution of chalcopyrite was investigated under atmospheric pressure, with sulfate media at low temperatures, in 30°C to 50°C. In the galvanic interaction between chalcopyrite and pyrite, pyrite is used as a leaching catalyst. Effects of different parameters such as temperature, stirring speed, pyrite to chalcopyrite ratio, particle size, and solution potential wer...

متن کامل

Dissolution Kinetic Evaluation of Manganese-rich Iron ore by Sulphuric acid Solution

This study investigated the optimum conditions for the leaching of manganese-rich iron ore for subsequent beneficiation studies in laboratory scale. The experiments were carried out by varying the concentration of H2 SO4 solution and the leaching temperature. The properties of the iron ore was characterized by X-ray fluorescence (XRF), X-ray diffraction (XRD), Scanning Electron Microscopy (SEM)...

متن کامل

Effect of Mechanical Activation on the Kinetics of Ammoniacal Thiosulfate Leaching of a Refractory Oxide Gold Ore

The effect of mechanical activation on the kinetics of ammoniacal thiosulfate leaching of a refractory oxide gold ore containing 2.8 ppm Au was investigated. The gold extraction of 99.81% was achieved by 16 h leaching of a sample mechanically activated for 60 minutes. The gold extraction observed for a similar reference sample without mechanical activation was only 55%. Studies revealed that le...

متن کامل

Preparation of nano silver powder from acid leaching tail in gold room

According to the unique properties and many applications of nano silver powder, it was prepared from acid leaching tail solution. The low value residual gold and silver ions were occurred with fellow heavy metals as pollutants (Fe2+, Cu 2+ and Zn2+) in acid leaching tail solution in Mouteh gold mine in Iran. Preparation of nano silver particles was achieved in two steps: first, by addition of a...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Journal of hazardous materials

دوره 121 1-3  شماره 

صفحات  -

تاریخ انتشار 2005