Synthesis and optical properties of co-doped ZnO submicrometer tubes from electrospun fiber templates.
نویسندگان
چکیده
Submicrometer ZnO tubes have been synthesized by a polymer based template approach using sol-gel deposition. Zinc acetate, a precursor to ZnO, was deposited on catalytically active electrospun polycarbonate fibers approximately 250+/-100 nm in diameter. Thermal degradation of the core fibers resulted in the oxidation of zinc acetate to produce ZnO nanotubes with diameters of approximately 500+/-100 nm and an average wall thickness of approximately 100+/-50 nm. Scanning electron microscopy (SEM), Energy dispersive spectroscopy, thermogravimetric analysis, Fourier transform infrared spectroscopy, and UV-visible spectroscopy were used to characterize the composition, structure, and morphology of the tubes. Powder X-ray diffraction results showed that a wurtzite crystalline phase was obtained. The UV-visible absorption spectrum was red-shifted by 25 nm due to narrowing of the ZnO band gap (approximately 3.22 eV) as a result of Co doping. Similarly, green band emission was not observed in the emission spectrum, while emission lifetime was determined to be 620 ps from photoluminescence studies.
منابع مشابه
Sonochemical synthesis of undoped and Co-doped ZnO nanostructures and investigation of optical and photocatalytic properties
In this paper, undopedZnO and Co-ZnOnano structureswith different molar ratio of Cobalt have been synthesized by the sonochemical method. Structure have been characterized by Fourier Transform (FTIR) and UV–Vis spectroscopy,Scanning Electron Microscopy (SEM), Energy Dispersive Analytical X-Ray (EDAX), and X-Ray Diffraction (XRD) methods. Moreover, the direct band gap has been calculated by Tauc...
متن کاملSonochemical synthesis of undoped and Co-doped ZnO nanostructures and investigation of optical and photocatalytic properties
In this paper, undopedZnO and Co-ZnOnano structureswith different molar ratio of Cobalt have been synthesized by the sonochemical method. Structure have been characterized by Fourier Transform (FTIR) and UV–Vis spectroscopy,Scanning Electron Microscopy (SEM), Energy Dispersive Analytical X-Ray (EDAX), and X-Ray Diffraction (XRD) methods. Moreover, the direct band gap has been calculated by Tauc...
متن کاملEffects of Cobalt Doping on Optical Properties of ZnO Thin Films Deposited by Sol–Gel Spin Coating Technique
Cobalt (Co) doped Zinc Oxide (ZnO) thin films, containing different amountof Cobalt nanoparticles as the Co doping source, deposited by the sol–gel spin coatingmethod onto glass via annealing temperature at 400˚C, have been investigated by opticalcharacterization method. The effect of Co incorporation on the surface morphology wasclearly observed from scanning electron microscopy (SEM) images. ...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملRoom Temperature Ferromagnetism in Cobalt Doped ZnO Nanoparticles
In this work we report synthesis and magnetic characterization of cobalt doped ZnO nanoparticles (with different percent of doped cobalt oxide). Synthesis of the materials was carried out at room temperature by polyacrylamide-gel method, using zink sulfate and cobalt nitrate as source materials, acrylamide as monomer and N,N-methylene bisacrylamide as a lattice reagent. Characterization of the ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Langmuir : the ACS journal of surfaces and colloids
دوره 25 13 شماره
صفحات -
تاریخ انتشار 2009