Tensile Properties of Hydroxyapatite Whisker Reinforced Polyetheretherketone

Polyetheretherketone (PEEK) was reinforced with 0-40 vol% hydroxyapatite (HA) whiskers using a novel powder processing and compression molding technique. A powder mixture was uniaxially pressed into a composite powder compact and compression molded into a flat composite bar using an open-channel die, such that the HA whiskers exhibited a preferred orientation along the length of the bar and tensile specimens. As expected, increased HA whisker reinforcement resulted in increased elastic modulus, but decreased ultimate tensile strength and strainor work-to-failure. PEEK reinforced with 40 vol% HA whiskers exhibited an elastic modulus of 16-18 GPa. PEEK reinforced with 20 vol% HA whiskers had an ultimate tensile strength of 70-80 MPa. Human cortical bone exhibits an elastic modulus of 17-26 GPa and an ultimate tensile strength of 80-150 MPa in the longitudinal direction (direction of principal stress). Stiffness coefficients measured by ultrasonic wave propagation indicated a level orthotropy also similar to that of human cortical bone tissue.