Mean Strain Effects and Microstructural Observations during In-vitro Fatigue Testing of Niti
نویسندگان
چکیده
The non-linear nature of the superelastic phase transformation in NiTi means that conventional fatigue life theory is difficult to apply. The volume fraction of martensite/parent phase and its role in the fatigue mechanism is not understood. This paper considers the fatigue life of superelastic NiTi alloys when tested at 2Hz in Ringers solution. In agreement with other researchers [1] [2] it was found that low alternating strains but high mean strain values resulted in the longest fatigue lives. To support the mechanical testing data, optical and electron microscopy was used to investigate the mechanism of fatigue and the role of the NiTi microstructure.
منابع مشابه
Detailed Microstructural Evolutions of TWIP Steel During Tensile Straining: In situ SEM Observations
Microstructural evolutions of twinning induced plasticity (TWIP) steel during tensile straining were investigated by in situ SEM observations. The results indicated that slip lines and mechanical twins as well as surface relief were increased with increasing strain, resulting in a stepped surface. Additionally, these deformation mechanisms could change the shape of each grain via shear and rota...
متن کاملFatigue crack-growth in shape-memory NiTi and NiTi–TiC composites
An experimental study was conducted to examine the room-temperature fatigue crack-growth characteristics of shape-memory NiTi matrix composites reinforced with 10 and 20 vol.% of TiC particles. Microstructural characterization of these hot-isostatically-pressed materials shows that the TiC particles do not react with the NiTi matrix and that they lack any texture. Overall fatigue crack-growth c...
متن کاملAbnormal Plastic Behavior of Fine Grain Mp35n Alloy During Room Temperature Tensile Testing
In this paper, results of an investigation on the strain hardening responses of superalloy MP35N with two average grain sizes of 38 and 1 μm, during room temperature tensile testing are reported. The microstructural evolution of the deformed samples was studied using optical and transmission electron microscopy (TEM) techniques. The strain hardening behavior of the 38 μm material was rather sim...
متن کاملCyclic Flexural Fatigue Resistance of the Revo-s Rotary Nickel-titanium Endodontic Files
Resistance to cyclic flexural fatigue failure is an important feature of rotary nickel-titanium (NiTi) instruments. The aim of this study was to evaluate the cyclic flexural fatigue failure resistance of RevoS Shaper Universal rotary NiTi files and to compare it to two other rotary NiTi files with similar size and taper, the Hero Shaper and the ProFile. Fifteen each of Revo-S Shaper Universal, ...
متن کاملPrediction of Fatigue Life in Notched Specimens Using Multiaxial Fatigue Criteria
In this research, the effects of notch shape on the fatigue strength of 2024-T3 aluminum alloy notched specimens have been studied using experimental and multiaxial fatigue analysis. For this purpose, four set of specimens with different notch shape were prepared and then fatigue tests were carried out at various cyclic longitudinal load levels. Load controlled fatigue tests of mentioned specim...
متن کامل