Preparation and Photocatalytic Activity of TiO2-Wrapped Cotton Nanofiber Composite Catalysts
نویسندگان
چکیده
A novel TiO2-wrapped nanofiber composite catalyst, which possessed a unique porous structure and mixed crystalline phase, was prepared by the combination of superficial sol–gel and post-calcination processes. By means of the superficial sol–gel process, TiO2 layers were deposited on the surface of each nanofiber-like cellulose fiber, and then the TiO2wrapped nanofiber composite catalysts were calcined at different temperatures under a nitrogen atmosphere. With temperature increasing, the original cotton nanofiber composites were converted into porous carbon nanofiber catalysts wrapped by a TiO2 mixed crystalline phase, which was accompanied by a crystal transformation. The photocatalytic activity of the new catalysts was evaluated by the degradation of methylene blue (MB) under ultraviolet (UV) irradiation. The results demonstrated that the new catalysts had good photocatalytic ability, and the TNC-700 catalyst showed a superior photocatalytic ability compared with the other catalysts; the new catalysts had a unique porous structure, high specific surface area, and mixed crystalline phase. Additionally, the synergistic photocatalytic effect of the TiO2 and activated carbon nanofiber resulted in the efficient degradation of organic pollutants in water or air.
منابع مشابه
Preparation of polyacrylonitrile – titania electrospun nanofiber and its photocatalytic dye degradation ability
In this paper, polyacrylonitrile PAN - titania TiO2 electrospun nanofiber PAN/TiO2 nanofiber was prepared via a facile electrospinning method. The characteristics of the PAN/TiO2 nanofiber were investigated using SEM and FTIR. The nanofiber showed retained nanofiber structures and high photocatalytic efficiency under UV light for the degradation of Direct Red 80 DR80 and Direct Red 23 DR23 in w...
متن کاملSynthesis, structural characterization and catalytic activity of TiO2/Al2O3 photo-composite
In recent years, the effects of heterogeneous catalysts for the oxidation of organic and inorganic pollutants in industrial wastewaters are spread. Traditionally, these reactions are usually carried out using suspensions of photo-catalysts such as TiO2. A chemical method including TiCl4, Al(NO3)3, ethanol amine, ethyl acetoacetate and aqueous ammonia were used for the fabrication of TiO2-Al2O3 ...
متن کاملEnhanced photocatalytic activity of fish scale loaded TiO2 composites under solar light irradiation.
Fish scale (FS) loaded TiO2 composites were investigated as photocatalysts in degradation of Methyl Orange under solar light irradiation. Composites were prepared through sol-gel method by varying mass ratio of TiO2/FS at 90:10, 70:30 and 50:50, respectively. The catalysts prepared in this study were characterized by using XRD, SEM, FT-IR and nitrogen sorption. The effects of solar irradiation,...
متن کاملPhotocatalytic Mineralization of Methylene BlueAqueous Solutions by Ag/TiO2 Nano Composite
Nanocomposite of Ag/TiO2 and nanocrystalline TiO2 were prepared by using TiCl4 as a precursor in a simple sol-gel process. The prepared photo-catalysts were characterized by X-ray diffraction (XRD), scanning electron micrographs (SEM), energy dispersive X-ray microanalysis (EDX), transmission electron microscopy (TEM) and diffuse reflectance spectroscopy (DRS). A complete and effective photocat...
متن کاملPreparation, characterization and photocatalytic behavior of WO3-fullerene/TiO2 catalysts under visible light
WO3-treated fullerene/TiO2 composites (WO3-fullerene/TiO2) were prepared using a sol-gel method. The composite obtained was characterized by BET surface area measurements, X-ray diffraction, scanning electron microscopy, energy dispersive X-ray analysis, transmission electron microscopy, and UV-vis analysis. A methyl orange (MO) solution under visible light irradiation was used to determine the...
متن کامل