A simple synthesis of mesoporous carbons with tunable mesopores using a colloidal template-mediated vapor deposition polymerization.
نویسندگان
چکیده
Mesoporous carbons with highly uniform and tunable mesopores were fabricated by one-step vapor deposition polymerization (VDP) using colloidal silica particles as templates and polyacrylonitrile (PAN) as a carbon precursor.
منابع مشابه
Ten Years of Research on Ordered Mesoporous Carbons: Major Advances in Synthesis, Properties and Potential Applications
About ten years ago Ryoo and co-workers [1,2] reported the hard-templating (HT) synthesis of ordered mesoporous carbons (OMCs) by using ordered mesoporous silicas (OMSs) as hard templates. Five years afterward the soft-templating (ST) synthesis of OMCs has been discovered [3-6]. Significant progress has been made in both hardand soft-templating synthesis of OMCs [7-10]. Major advances in the sy...
متن کاملHierarchical Phenolic Resin-based Carbons with High Surface Area and Pore Volume Obtained by Soft-templating and Activation
Introduction Advanced applications often require carbons with high surface area and hierarchical porous structures. In response to this demand some efforts have been undertaken to create materials, which effectively combine the properties of both activated carbons (high surface area) and ordered mesoporous carbons (tunable and well-developed porosity). While there are activation methods, which ...
متن کاملA facile synthesis of polypyrrole nanotubes using a template-mediated vapor deposition polymerization and the conversion to carbon nanotubes.
Polypyrrole (PPy) nanotubes with highly uniform surface and tunable wall thickness were fabricated by one-step vapor deposition polymerization (VDP) using anodic aluminium oxide (AAO) template membranes, and transformed into carbon nanotubes through a carbonization process.
متن کاملIntegrated structural control of cage-type mesoporous platinum possessing both tunable large mesopores and variable surface structures by block copolymer-assisted Pt deposition in a hard-template.
Cage-type mesoporous Pt with tunable large mesopores possessing smooth and rough pore surfaces were prepared selectively by the deposition of Pt in the absence and presence of a block copolymer in a hard-template, respectively.
متن کاملTemplate Synthesis of Three-Dimensional Cubic Ordered Mesoporous Carbon With Tunable Pore Sizes
Three-dimensional cubic ordered mesoporous carbons with tunable pore sizes have been synthesized by using cubic Ia3d mesoporous KIT-6 silica as the hard template and boric acid as the pore expanding agent. The prepared ordered mesoporous carbons were characterized by powder X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and nitrogen adsorption-desorption anal...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 33 شماره
صفحات -
تاریخ انتشار 2005