Synthesis of Y2O3:Bi3+,Eu3+ nanosheets from layered yttrium hydroxide precursor and their photoluminescence properties
نویسندگان
چکیده
Department of Applied Chemistry, Faculty of 3-14-1 Hiyoshi, Kohoku-ku, Yokohama 223-8 [email protected]; Fax: + 81 45 566 155 † Electronic supplementary information ( undoped, 10 at% Bi-doped, and 2 a high-precision (220) XRD peaks and (2 Bi-doped, 2 at% Eu-doped, and Bi,E samples, respectively (Fig. S2); calculated Fig. S2 (Tables S1 and S2); AFM images a Y2O3 nanosheet, codoped with 10 at% proles, atomic compositions determined at% Bi,2 at% Eu-codoped Y2O3 sam respectively). See DOI: 10.1039/c7ra01114 Cite this: RSC Adv., 2017, 7, 14107
منابع مشابه
A facile synthesis of strong near infrared fluorescent layered double hydroxide nanovehicles with an anticancer drug for tumor optical imaging and therapy.
In this work, a new multifunctional nanovehicle for tumor optical imaging and therapy was developed using Y2O3:Er(3+),Yb(3+) nanoparticles as near infrared fluorescent nanophosphors, and MgAl-layered double hydroxide (LDH) nanosheets as anticancer drug nanovehicles. Monodispersed Y2O3:Er(3+),Yb(3+) nanophosphors were readily synthesized by the urea assisted homogenous precipitation method. Hier...
متن کاملSynthesis and photoluminescence properties of layered oxides intercalated with Eu3+ ions by electrostatic self-assembly method using oxide nanosheets
Layered oxides intercalated with Eu ions were prepared by self-assembly deposition method based on the electrostatic interaction between negative charged oxide nanosheets and Eu ions. The layered oxides were composed of two-dimensional host nanosheet layer with guest Eu ions and gave Eu emission based on an energy transfer from bandgap excitation of the host oxide nanosheets to the Eu ions. The...
متن کاملPreparation and photoluminescence of yttrium hydroxide and yttrium oxide doped with europium nanowires
Single-crystalline Y(OH)3:Eu nanowires have been prepared by polymer-assisted hydrothermal method. The yields of the nanowires were higher than 95%. XRD patterns showed that the products were the hexagonal Y(OH)3 structure. SEM images displayed that the nanowires consisted of nanobelts and nanorods. The nanorods have the diameter of about 85 nm and length up to several tens of microns, and the ...
متن کاملCombinatorial study of the optimization of Y2O3:Bi,Eu red phosphors.
The present investigation aims at the synthesis of (Y2-xEuxBiy)O3 red phosphor materials using the combinatorial chemistry method. We developed square-type arrays consisting of 90 compositions to obtain the optimum composition of co-dopants in a Y2O3 host. The optimized composition was found to be (Y2-xEuxBiy)O3 (x = 0.16-0.18, y = 0.08-0.10). The screening of the compositions was investigated ...
متن کاملTens of micron-sized unilamellar nanosheets of Y/Eu layered rare-earth hydroxide: efficient exfoliation via fast anion exchange and their self-assembly into oriented oxide film with enhanced photoluminescence
Layered rare-earth hydroxide (LRH) crystals of (Y0.95Eu0.05)2(OH)5NO3·nH2O with a lateral size of ∼ 300 μm and a thickness of ∼ 9 μm have been synthesized via a hydrothermal reaction of mixed nitrate solutions in the presence of mineralizer NH4NO3 at 200 °C for 24 h. LRH exhibits the ability to undergo intercalation and anion exchange with DS- (C12H25OSO3-) via hydrothermal treatment. Compared ...