CVD growth of 3C-SiC on 4H-SiC substrate

نویسندگان

  • Anne Henry
  • Xun Li
  • Stefano Leone
  • Olof Kordina
  • Erik Janzén
چکیده

The hetero epitaxial growth of 3C-SiC on nominally on-axis 4H-SiC is reported. A horizontal hot-wall CVD reactor working at low pressure is used to perform the growth experiments in a temperature range of 1200-1500 °C with the standard chemistry using silane and propane as precursors carried by a mix of hydrogen and argon. The optimal temperature for single-domain growth is found to be about 1350 °C. The ramp up-conditions and the gas-ambient atmosphere when the temperature increases are key factors for the quality of the obtained 3C layers. The best pre-growth ambient found is carbon rich environment; however time of this pre-treatment is crucial. A too high C/Si ratio during growth led to polycrystalline material whereas for too low C/Si ratios Si cluster formation is observed on the surface. The addition of nitrogen gas is also explored.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Advances in the molecular-beam epitaxial growth of artificially layered heteropolytypic structures of SiC

The controlled growth of SiC heteropolytypic structures consisting of hexagonal and cubic polytypes has been performed by solid-source molecular-beam epitaxy. On on-axis substrates, 4H/3C/4H–SiC~0001! and 6H/3C/6H–SiC~0001! structures were obtained by first growing the 3C–SiC layer some nanometer thick at lower substrate temperatures (T51550 K) and Si-rich conditions and a subsequent growth of ...

متن کامل

4H-SiC Epitaxial Layers Grown on on-axis Si-face Substrate

We report on the growth of 4H-SiC epitaxial layer on Si-face polished nominally on-axis 2” full wafer, using Hot-Wall CVD epitaxy. The polytype stability has been maintained over the larger part of the wafer, but 3C inclusions have not been possible to avoid. Special attention has given to the mechanism of generation and propagation of 3C polytype in 4H-SiC epilayer. Different optical and struc...

متن کامل

Suppression of 3C-Inclusion Formation during Growth of 4H-SiC Si-Face Homoepitaxial Layers with a 1° Off-Angle

We grew epitaxial layers on 4H-silicon carbide (SiC) Si-face substrates with a 1° off-angle. The suppression of 3C-inclusion formation during growth at a high C/Si ratio was investigated, because a growth technique with a high C/Si ratio is needed to decrease residual nitrogen incorporation. 3C inclusions were generated both at the interface between the substrate and epitaxial layer, and during...

متن کامل

Chloride based CVD of 3C-SiC on (0001) α-SiC substrates

A chloride-based chemical-vapor-deposition (CVD) process has been successfully used to grow very high quality 3C-SiC epitaxial layers on on-axis α-SiC substrates. An accurate process parameters study was performed testing the effect of temperature, in situ surface preparation, precursor ratios, nitrogen addition, and substrate polytype and polarity. The 3C layers deposited showed to be largely ...

متن کامل

Sublimation Growth and Performance of Cubic Silicon Carbide

Current advancement in electronic devices is so rapid that silicon, the semiconductor material most widely used today, needs to be replaced in some of the fields. Silicon carbide (SiC) is a wide band gap semiconductor satisfying requirements to replace silicon in devices operating at high power and high frequency at elevated temperature, and in harsh environments. Hexagonal polytypes of SiC, su...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2012