Synthesis and structure of Bi2Ce2O7: a new compound exhibiting high solar photocatalytic activity.
نویسندگان
چکیده
A facile method of solution combustion was used to synthesize a new solid solution Bi(2)Ce(2)O(7). The structure was determined from powder X-ray diffraction (PXRD) and found to crystallize in the space group Fm3m with cell parameter a = 5.46936(9) Å. The particle sizes varied from 5 to 6 nm. The degradation of cationic dye malachite green (MG) was investigated under solar radiation as the band gap of the material is 2.34 eV.
منابع مشابه
Room Temperature Synthesis of N-doped Urchin-like Rutile TiO2 Nanostructure With Enhanced Photocatalytic Activity Under Sunlight
We report the synthesis of nitrogen-doped urchin-like rutile TiO2 nanostructure at room temperature without further heat treatment. The process was operated through hydrolysis of Ti(OC4H9)4 employing the direct amination of the product. The samples characterized by x-ray diffraction (XRD), scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Raman spectroscopy and Brunaue...
متن کاملUsing the [Co(oct)2] as a New Precursor for Simple Synthesis of CoS2 Nanoparticles and Kinetics Studies on Photocatalytic Activities Under UV Irradiation
Cobalt sulfide (CoS2) nanostructures were synthesized via a simple thermal decomposition method using [Co(oct)2] as a new precursor. Using the organometallic compound as precursor could synthesize materials in nano-scale because of having the massive structure that acted as capping agent. The products were characterized by various analyses such as X-ray diffraction pattern (XRD), scanning elect...
متن کاملSynthesis and photocatalytic activity of nanosized modified mesocellulous silica foams (MCFs) with PW12 and vanadium oxide
A series of tungestophosphoric acid and vanadium oxide supported on Mesocellulous Silica Foams (MCFs) featuring a well-defined three-dimensional (3D) mesoporosity were studied with regard to their performance in the photocatalytic activity to degrade Oezine Y (OY). This nanosized mesoporous catalyst (PW12@V-MCF) was characterized by FTIR, XRD, BET and TEM. XRD shows that the structure of MCF re...
متن کاملSynthesis and photocatalytic activity of nanosized modified mesocellulous silica foams (MCFs) with PW12 and vanadium oxide
A series of tungestophosphoric acid and vanadium oxide supported on Mesocellulous Silica Foams (MCFs) featuring a well-defined three-dimensional (3D) mesoporosity were studied with regard to their performance in the photocatalytic activity to degrade Oezine Y (OY). This nanosized mesoporous catalyst (PW12@V-MCF) was characterized by FTIR, XRD, BET and TEM. XRD shows that the structure of MCF re...
متن کاملSolar Photocatalytic Degradation of Diclofenac by N-Doped TiO2 Nanoparticles Synthesized by Ultrasound
Anatase N-doped TiO2 nanoparticles were synthesized using ultrasound at low frequency and room temperature. The samples characterized by techniques including XRD, TEM, HRTEM, FT-IR, XPS, and UV–Vis spectroscopy. XPS indicated the existence of nitrogen as an anion dopant within the TiO2 lattice. The solar photocatalytic activity of N-doped TiO2 studied for th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Dalton transactions
دوره 41 32 شماره
صفحات -
تاریخ انتشار 2012