Wide-Range Magnetoelectric Response on Hybrid Polymer Composites Based on Filler Type and Content

نویسندگان

  • Pedro Martins
  • Marco Silva
  • Silvia Reis
  • Nélson Pereira
  • Senentxu Lanceros-Mendez
  • Joannis K. Kallitsis
  • Georgios Bokias
چکیده

In order to obtain a wide-range magnetoelectric (ME) response on a ME nanocomposite that matches industry requirements, Tb0.3Dy0.7Fe1.92 (Terfenol-D)/CoFe2O4/P(VDF-TrFE) flexible films were produced by the solvent casting technique and their morphologic, piezoelectric, magnetic and magnetoelectric properties were investigated. The obtained composites revealed a high piezoelectric response (≈−18 pC·N−1) that is independent of the weight ratio between the fillers. In turn, the magnetic properties of the composites were influenced by the composite composition. It was found that the magnetization saturation values decreased with the increasing CoFe2O4 content (from 18.5 to 13.3 emu·g−1) while the magnetization and coercive field values increased (from 3.7 to 5.5 emu·g−1 and from 355.7 to 1225.2 Oe, respectively) with the increasing CoFe2O4 content. Additionally, the films showed a wide-range dual-peak ME response at room temperature with the ME coefficient increasing with the weight content of Terfenol-D, from 18.6 to 42.3 mV·cm−1·Oe−1.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Epoxy Resin Composite Based on Functional Hybrid Fillers

A study was carried out involving the filling of epoxy resin (EP) with bentonites and silica modified with polyhedral oligomeric silsesquioxane (POSS). The method of homogenization and the type of filler affect the functional and canceling properties of the composites was determined. The filler content ranged from 1.5% to 4.5% by mass. The basic mechanical properties of the hybrid composites we...

متن کامل

The Electrical Properties of Hybrid Composites Based on Multiwall Carbon Nanotubes with Graphite Nanoplatelets

In the present work, we have investigated the concentration dependences of electrical conductivity of monopolymer composites with graphite nanoplatelets or multiwall carbon nanotubes and hybrid composites with both multiwall carbon nanotubes and graphite nanoplatelets. The latter filler was added to given systems in content of 0.24 vol%. The content of multiwall carbon nanotubes is varied from ...

متن کامل

Preparation and Characterization of Eco-Friendly Mg(OH)2/Lignin Hybrid Material and Its Use as a Functional Filler for Poly(Vinyl Chloride)

A functional magnesium hydroxide/lignin hybrid system was prepared by grinding and mixing the pure precursors using a planetary ball mill. In addition, the thermal stability was assessed based on the total mass loss of the hybrid system within the temperature range of 30–1000 ◦C, which amounted to 38%. Moreover, the average particle size was at 4.9 μm as determined by the laser diffraction meth...

متن کامل

Statistical Analysis and Predictive Learning of Mechanical Parameters for TiO2 Filled GFRP Composite

The new, polymer composites consisting of e-glass fiber reinforcement with titanium oxide filler in the double bonded unsaturated polyester resin matrix were made. The glass fiber and titanium oxide reinforcement composites were made in three different fiber lengths (3cm, 5cm, and 7cm), filler content (2 wt%, 4 wt%, and 6 wt%) and fiber content (20 wt%, 40 wt%, and 60 wt%). 27 different composi...

متن کامل

Influence of ferrite nanoparticle type and content on the crystallization kinetics and electroactive phase nucleation of poly(vinylidene fluoride).

This work reports on the nucleation of the β-phase of poly(vinylidene fluoride) (PVDF) by incorporating CoFe(2)O(4) and NiFe(2)O(4) nanoparticles, leading in this way to the preparation of magnetoelectric composites. The fraction of filler nanoparticles needed to produce the same β- to α-phase ratio in crystallized PVDF is 1 order of magnitude lower in the cobalt ferrite nanoparticles. The inte...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2017