Preparation of YBa2Cu3O7−δ superconducting thick film on Ni−W tapes via electrophoretic deposition
نویسندگان
چکیده
The preparation of La0.4Sr0.6TiO3 (LSTO) buffer layer and YBa2Cu3O7−δ (YBCO) superconducting thick film by a low cost technology was studied. The crystal orientation of LSTO and YBCO films was detected by X-ray diffraction, the conductivity of LSTO film and superconductivity of YBCO coating were investigated by standard four-probe method. Excellent in-plane alignment, smooth and dense LSTO buffer layer was successfully prepared on textured Ni−W taps by metal organic deposition (MOD). YBCO thick film was fabricated by electrophoretic deposition (EPD). The effects of applied voltage and deposition time on the YBCO coatings properties were studied. The results show that the critical current density of the YBCO coating deposited under 138 V for 35 min was about 600 A/cm (0 T, 77 K).
منابع مشابه
Effect of Sintering Conditions on Microstructure and the Superconducting Properties of YBa2Cu3O7 x
YBa2Cu3O7-X tapes fabricated from precursor powder, were used to investigate the effect of sintering conditions on the microstructure. The sintering experiments were carried out in oxygen over the temperature range of 915-950ْC. Scanning electron microscopy was used to examine the sintered products. The result indicated a significant increase in densification and grain growth when the tapes were...
متن کاملChemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes
CeO2/La2Zr2O7 composite buffer layers were deposited on Ni-W tapes using chemical solution method. YBa2Cu3O7-x (YBCO) films were then deposited on the CeO2/La2Zr2O7 composite buffer layers using a low-fluorine solution route. Effect of the annealing temperature and annealing atmosphere on the texture of the CeO2 layers was investigated. It was found that CeO2 film annealed at 1000°C under the a...
متن کاملMechanisms of weak thickness dependence of the critical current density in strong-pinning ex situ metal–organic-deposition-route YBa2Cu3O7−x coated conductors
We report on the thickness dependence of the superconducting characteristics including critical current Ic, critical current density Jc, transition temperature Tc, irreversibility field Hirr, bulk pinning force plot Fp(H), and normal state resistivity curve ρ(T ) measured after successive ion milling of ∼1 μm thick high-Ic YBa2Cu3O7−x films made by an ex situ metal–organic deposition process on...
متن کاملEPITAXIAL YBa 2 Cu 307 ON BIAXIALLY TEXTURED ( 001 ) NI : AN APPROACH TO HIGH CRITICAL CURRENT DENSITY SUPERCONDUCTING TAPES
In-plane aligned, c-axis oriented YBazCu307 (YBCO) films with superconducting critical current densities, Jc, as high as 700,000 amperes per square centimeter at 77 kelvin have been grown on thermo-mechanically, rolled-textured (00 1) Ni tapes using pulsed-laser deposition. Epitaxial growth of oxide buffer layers directly on biaxially textured Ni, formed by recrystallization of cold-rolled pure...
متن کاملThick Film Deposition of Carbon Nanotubes by Alternating Electrophoresis
Electrophoretic deposition of carbon nanotubes (CNTs) using alternating current electric fields (0.01-1000 Hz) is reported. Pure acetone was used as suspending medium. Two parallel gold electrodes were used as depositing substrate. The effect of depositing parameters such as frequency and three waveforms (sinusoidal, rectangular and triangular) on deposit yield was investigated. According to ou...