Polymerization of a diacetylenic phospholipid monolayer at the air-water interface

Monolayers of a polymerizable phospholipid on water have been studied both before and after polymerization. Before polymerization, the phase diagram is established by isotherm measurements and optical microscopy (epifluorescence and direct observation between crossed polarizer and analyzer). This allows us to bring into evidence a coexistence region between a condensed and an expanded phase, above a triple point temperature Tt # 20 ° C. The dramatic influence of impurities on the size of coexistence domains between the condensed phase and the expanded one is clearly demonstrated, even at a very low concentration of impurities. Structural and morphological modifications during the polymerization were investigated using X-ray surface scattering together with atomic force microscopy. Whatever the polymerization conditions (constant area or constant pressure), X-ray reflectivity clearly shows the reorientation of the diacetylenic links. Only constant area polymerization leads to a viscoelastic behavior of the film, as shown by talcum decoration. The topochemical nature of the polymerization of