The obtaining of high-density specimens and analysis of mechanical strength characteristics of a composite based on ZrO2-WC nanopowders
نویسندگان
چکیده
The structures, processes of shrinkage, and phase composition of the compact system ZrO2-WC, obtained by hot pressing with the transmission of high current, are considered in the article. We found that as a result of compaction, the ZrO2-WC-ceramics have uniform density distribution, with the following optimal mode consolidation values T = 1,350°C, P = 30 MPa and t = 2 min. These conditions allow us to achieve the best combination of ceramic properties by criteria density and strength.
منابع مشابه
Study of milling effect on particle size and mechanical properties of WC-Co composite
The effect of milling on the particle size and mechanical properties Tungsten Carbide - Cobalt composite were investigated. First, raw materials ratios by mechanical milling for 4 hours at 300 rpm were mixed. The powder in the optimum temperature 1350°C at a rate of temperature rise 50°C / min and shelf life of 4 minutes and the pressure MPa 30 were sintered in SPS. The results indicated nearly...
متن کاملساخت و بررسی خواص نانوکامپوزیت کربن/فنولیک با استفاده از روش پیرولیز پلیمر و تقویت آن با نانوذرات اکسید فلزی
Carbon fiber composite is one of the most important materials in aerospace engineering applications. For fabrication of this composite, optimum polymerization and carbonization cycles of phenolic resin were obtained [1]. Then, carbon/phenolic composite was fabricated by mixing different weight percentages of T700 carbon fiber with phenolic resin, and the flexural strength of specimens was exami...
متن کاملInfluence of electroplating parameters on microstructure and amount of ceramic particle deposition in Ni-Co-CeO2-ZrO2 composite coating
Austenitic stainless steels are high performance steels that have various applications in solid oxide fuel cells and boiler tubes under high temperature operating conditions. The Cr2O3 oxide layer formed on the steel surface becomes unstable at high temperatures and reduces the oxidation resistance of the steel. Therefore, protection of these steels at high temperatures is essential. Therefore,...
متن کاملThe Effect of External Skin on Buckling Strength of Composite Lattice Cylinders Based on Numerical and Experimental Analysis
Currently, lattice composite structures have many applications in aerospace industries. The present research analyzed the effect of an external skin consisting of a lattice’s cylindrical shell on the buckling strength of composite materials, both numerically and experimentally. Two classes of specimens, with and without external skins, were fabricated using the filament winding process. To find...
متن کاملThe Impact of Current Density of Electroplating on Microstructure and Mechanical Properties of Ni-ZrO2-TiO2 Composite Coating
Metallic composite coatings with ceramic particles can be used to improve the mechanical and corrosion properties of steel. In the present research, Ni-ZrO2-TiO2 composite coating was fabricated on AISI 430 stainless steel through the electrodeposition method. The effect of the current density of electroplating (15, 17, 20, and 23 mA.cm-2)was investigated on the...
متن کامل