Diffraction Measurements of Load Transfer in Interpenetrating-Phase Al O /Al Composites
نویسندگان
چکیده
Interpenetrating Al O /Al composites were created by liquid metal infiltration of alumina structures with three-dimensional periodicity produced by a robotic deposition method. Volume-averaged lattice strains in the alumina phase were measured by synchrotron X-ray diffraction at various uniaxial compression stresses up to 200 MPa. Load transfer was observed to occur from the aluminum to the alumina phase, and the average state of stress in the alumina is close to uniaxial compression. No change in load transfer was observed upon unloading from 200 MPa, indicating that damage (by alumina fracture or interface decohesion) was absent. 2 3
منابع مشابه
Load partitioning in Al2O3–Al composites with three-dimensional periodic architecture
Interpenetrating composites are created by infiltration of liquid aluminum into three-dimensional (3-D) periodic Al2O3 preforms with simple tetragonal symmetry produced by direct-write assembly. Volume-averaged lattice strains in the Al2O3 phase of the composite are measured by synchrotron X-ray diffraction for various uniaxial compression stresses up to 350 MPa. Load transfer, found by diffrac...
متن کاملCorrosion Polarization Behavior of Al-SiO2 Composites in 1M and Related Microstructural Analysis
The composites combining aluminum and silica nanoparticles with the addition of tetramethylammonium hydroxide (Al-SiO2(T)) and butanol (Al-SiO2(B)) as mixing media have been successfully fabricated. Corrosion behavior of Al-SiO2 composites before and after exposure in 1M NaCl solution was examined using potentiodynamic polarization (Tafel curve analysis). The st...
متن کاملCOMPARISON OF MECHANICAL AND ELECTRICAL PROPERTIES OF PIEZOELECTRIC COMPOSITES PZT/ZnO AND PZT/Al FABRICATED BY POWDER METALLURGY
Lead zirconate titanate (PZT) as a piezoelectric ceramic has been used widely in the fields of electronics, biomedical engineering, mechatronics and thermoelectric. Although, the electrical properties of PZT ceramics is a major considerable, but the mechanical properties such as fracture strength and toughness should be improved for many applications. In this study, lead monoxide, zirconium ...
متن کاملThermochemical Heat Storage Properties of Co3O4-X wt % Al2O3 and Co3O4-X wt % Y2O3 Composites (X=1, 2, 5, 8, 10)
The effect of Al2O3 (1-10 wt %) and Y2O3 (1-10 wt %) additions on thermochemical heat storage properties of Co3O4/CoO system was investigated by thermogravimetry, XRD, and SEM analyses. Results showed that the addition of Al2O3 to Co3O4 at constant 8 h mechanical activation improved the...
متن کاملThe Effect of TiC Additive with Al2O3-Y2O3 on the Microstructure and Mechanical Properties of SiC Matrix Composites
In this research, the SiC-matrix composite with different amounts of TiC (0, 2.5, 5, 7.5, and 10 wt%) supplemented with additives including 4.3 wt% Al2O3 and 5.7 wt% Y2O3 were utilized to initiate the required liquid phase. The sintering process was performed using pressureless sintering at 1900 °C for 1.5 hours under argon atmosphere. The compos...
متن کامل