Fe-Al-C carbide phase nano-layer investigation as a substrate for epitaxial diamond growth
نویسنده
چکیده
Calculations of electron structure of supercells consisting of several layers of ordinary stoichiometric K-phase and modified K-phase, on which according to our assumptions epitaxial growth of diamonds is possible, were conducted. Stability of calculated cells was considered, and optimal number of layers of the stoichiometric K-phase in the supercell was determined in order for it to be thermodynamically stable. Electronic structure of carbon in the modified K-phase layer was considered and compared to electron structure of carbon in diamond.
منابع مشابه
Substantiation of Epitaxial Growth of Diamond Crystals on the Surface of Carbide Fe3AlC0.66 Phase Nanoparticles
Samples of Fe-Al-C alloys of varying composition were synthesized under high pressures and temperatures. From X-ray analysis data, only K-phase with usual for it average parameter of elemental lattice cell, a = 0.376 nm, carbide Fe3C and cubic diamond reflexes were present before and after cooling to the temperature of liquid nitrogen.Calculations were made of the parameters of unit cells, the ...
متن کاملSuppression of 3C-Inclusion Formation during Growth of 4H-SiC Si-Face Homoepitaxial Layers with a 1° Off-Angle
We grew epitaxial layers on 4H-silicon carbide (SiC) Si-face substrates with a 1° off-angle. The suppression of 3C-inclusion formation during growth at a high C/Si ratio was investigated, because a growth technique with a high C/Si ratio is needed to decrease residual nitrogen incorporation. 3C inclusions were generated both at the interface between the substrate and epitaxial layer, and during...
متن کاملA quasi-equilibrium model for the prediction of interlayer chemistry during diamond chemical vapor deposition
The chemistry of the intermediate layer that develops at the interface between diamond and a non-diamond substrate during diamond chemical vapor deposition is analyzed using a thermodynamic quasi-equilibrium model. Substrates of Si, Mo, W, Ti, Ta, Fe and Ni are examined, and the physical parameters such as substrate temperature, reactor pressure, and CH rH ratio in the gas phase required for 4 ...
متن کاملOn the Investigation of Sol-Gel TiO2 Nanostructured Films Applied on Windshields Pre-Coated with SiO2 Layer by Dip-Coating Method
TiO2-SiO2 photocatalytic nanostructure film on windshield for self-cleaning purposes was prepared via sol–gel dip-coating method. TiO2 films were prepared on automotive glass pre-coated with a SiO2 layer by a dip-coating method followed by annealing at 500 °C for 30min. The films were characterized using X-ray diffraction XRD and scanning electron microscopy SEM, FE-SEM techniques. The TiO2-SiO...
متن کاملThe Growth of Diamond-like Carbon Nano-Structures: Investigation of the Affecting Factors
Using DC-Plasma Enhanced Chemical Vapour Deposition (PECVD) system, the impact of pure Co onthe growth of diamond-like carbon (DLC) nano-structures were investigated. In this study, Acetylene(C2H2) was diluted in H2 and used as the reaction gas and Cobalt (Co) nano-particles were used asthe catalyst. The effect of preparing Co catalyst at temperatures of 240°C and 350°C and growthconditions was...
متن کامل