Comparative Studies on Ultraviolet-Light-Derived Photoresponse Properties of ZnO, AZO, and GZO Transparent Semiconductor Thin Films

نویسندگان

  • Chien-Yie Tsay
  • Wei-Tse Hsu
چکیده

ZnO, Al-doped ZnO (AZO), and Ga-doped ZnO (GZO) semiconductor thin films were deposited on glass substrates via a sol-gel spin-coating process for application in a photoconductive ultraviolet (UV) detector. The doping concentrations of Al and Ga were 1.0 at % in the precursor solutions. In this study, the microstructural features and the optical and electrical properties of sol-gel-derived ZnO, AZO, and GZO thin films were compared, and the performance of ZnO-based UV photodetectors under ultraviolet A (UVA) light were measured. Experimental results confirmed the synthesis of single-phase nanocrystalline ZnO-based thin films and the successful substitution of Al and Ga into Zn sites in ZnO crystals. The results also demonstrated that the optical transmittance and electrical properties of ZnO thin films could be improved by Al and Ga doping. UV photodetectors based on ZnO-based thin films, having a metal-semiconductor-metal (MSM) configuration, were fabricated with Al inter-digitated electrodes. All photodetectors showed an ohmic nature between semiconductor and electrode contacts and exhibited a sharp increase in photocurrent under illumination with UVA light. We found that the MSM UV photodetector based on the GZO semiconductor thin film exhibited the best UV response (IUVA/Idark) of 73.3 and the highest photocurrent responsivity of 46.2 A/W under UVA light (power density ~0.825 mW/cm²) at 5 V bias.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

The Microstructure of Aging ZnO, AZO, and GZO Films

RF magnetron sputtering is used on the ceramic targets, each of which contains zinc oxide (ZnO), zinc oxide doped with aluminum (AZO) and zinc oxide doped with gallium (GZO). The electric conduction mechanism of the AZO and GZO films came mainly from the Al and Ga, the oxygen vacancies, Zn interstitial atoms, and Al and/or Ga interstitial atoms. AZO and GZO films achieved higher conduction than...

متن کامل

Preparation and Characterization of ZnO Thin Layers with Various Percentages of Gallium Impurities

In this study, thin films of pure ZnO and  doped ZnO with different percentages of gallium (0.5, 1, 2 and 4vt. %) on the glass substrates were deposited by using sol-gel method via spin coating technique at 2500 rpm, and all layers were annealed at 200°C for 1h and then Were examined their electrical, optical and structural properties. Concentration of all solution was 0.1M. The results show th...

متن کامل

Spin-coated Ga-doped ZnO transparent conducting thin films for organic light-emitting diodes

Gallium doped zinc oxide (GZO) thin films have been prepared by a simple sol–gel spin coating technique. XRD results showed the preferential c-axis orientation of the crystallites and the presence of the wurtzite phase of ZnO. A lowest resistivity of 3.3 × 10−3 cm was obtained for the ZnO film doped with 2 at% of Ga after post-annealing at 500 ◦C for 45 min in a H2 atmosphere. All the films sho...

متن کامل

Ultraviolet detectors based on annealed zinc oxide thin films: epitaxial growth and physical characterizations

In this report, ultraviolet (UV) detectors were fabricated based on zinc oxide thin films. The epitaxial growth of zinc oxide thin films was carried out on bare glass substrate with preferred orientation to (002) plane of wurtzite structure through radio frequency sputtering technique. The structural properties indicated a dominant peak at 2θ=34.28º which was matched with JCPDS reference card N...

متن کامل

Comparative studies of Al-doped ZnO and Ga-doped ZnO transparent conducting oxide thin films

We have investigated the influences of aluminum and gallium dopants (0 to 2.0 mol%) on zinc oxide (ZnO) thin films regarding crystallization and electrical and optical properties for application in transparent conducting oxide devices. Al- and Ga-doped ZnO thin films were deposited on glass substrates (corning 1737) by sol-gel spin-coating process. As a starting material, AlCl3⋅6H2O, Ga(NO3)2, ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 10  شماره 

صفحات  -

تاریخ انتشار 2017