Thermoelectric Properties of Nano-Meso-Micro β-MnO2 Powders as a Function of Electrical Resistance
نویسندگان
چکیده
Particle sizes of manganese oxide (β-MnO2) powders were modified by using a mortar and pestle ground method for period of times that varied between 15-60 min. Particle size versus ground time clearly shows the existence of a size-induced regime transition (i.e., regime I and II). Thermoelectric properties of β-MnO2 powders as a function of electrical resistance in the range of R P = 10 - 80Ω were measured. Based on the data presented, we propose a model for the β-MnO2 system in which nanometer-scale MnO2 crystallites bond together through weak van der Waals forces to form larger conglomerates that span in size from nanometer to micrometer scale.
منابع مشابه
Effect of milling time and microwave sintering on microhardness and electrical properties of nano and micro structured cordierite
The purpose of this research is to investigate the mechanical and electrical properties of nano structured cordierite. Nano grain size powders were synthesized through mechanical activation by high-energy ball milling of the starting powders containing 34.86 wt% Al2O3, 51.36 wt% SiO2, and 13.78 wt% MgO. Samples were prepared by conventional and microwave sintering at 1390°C. SEM observations il...
متن کاملInvestigation on Mechanical and Electrical Properties of Cu-Ti Nanocomposite Produced by Mechanical Alloying
In this paper, Cu-Ti nanocomposite synthesized via ball milling of copper-titanium powders in 1, 3, and 6 of weight percentage compounds. The vial speed was 350 rpm and ball to powder weight ratio kept at 15:1 under Argon atmosphere, and the time of milling was 90 h. Obtained powders were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), and dynamic light scattering (DLS)....
متن کاملMechanical properties of SEVA / hydroxyapatite composite with to HAP different particle sizes
Hydroxyapatite is a biocompatible ceramic and reinforcement for bone implantations. SEVA/HAP composite content HAP filler with difference particle sizes were designed. Mechanical tests like tensile modulus, UTS, strain at break and biodegradation were investigated. Results illustrated much increase tensile modulus of composites content HAP nano powders ratio to micro powders. Also UTS analysis ...
متن کاملMechanical properties of SEVA / hydroxyapatite composite with to HAP different particle sizes
Hydroxyapatite is a biocompatible ceramic and reinforcement for bone implantations. SEVA/HAP composite content HAP filler with difference particle sizes were designed. Mechanical tests like tensile modulus, UTS, strain at break and biodegradation were investigated. Results illustrated much increase tensile modulus of composites content HAP nano powders ratio to micro powders. Also UTS analysis ...
متن کاملEFFECTS OF LANTHANUM DOPING ON THE ELECTRICAL PROPERTIES OF SOL-GEL DERIVED AND MECHANICALLY ACTIVATED Pb1.1- X LaX (Zr0.53Ti0.47) O3, NANO POWDERS
Abstract: The PZT-based ceramics with a composition of Pb1.1-xLax (Zr0.53Ti0.47)O3, were prepared by conventional mixed oxide followed by mechanical alloying and sol-gel methods in which x was chosen in the range of 0.02–0.06. The samples were calcined in the range of 450 °C - 750 °C for 4h. The physical and electrical properties of the samples were determined as a function of the calcinati...
متن کامل