Preparation and Isothermal Oxidation Behavior of Zr-Doped, Pt-Modified Aluminide Coating Prepared by a Hybrid Process
نویسندگان
چکیده
To take advantage of the synergistic effects of Pt and Zr, a kind of Zr-doped, Pt-modified aluminide coating has been prepared by a hybrid process, first electroplating a Pt layer and then co-depositing Zr and Al elements by an above-the-pack process. The microstructure and isothermal oxidation behavior of the coating has been studied, using a Pt-modified aluminide coating as a reference. Results showed that the Zr-doped, Pt-modified aluminide coating was primarily composed of β-(Ni,Pt)Al phase, with small amounts of PtAl2and Zr-rich phases dispersed in it. The addition of Zr diminished voids on the coating surface since Zr could hinder the growth of β-NiAl grains. It also helped to increase the spalling resistance of the oxide scale and reduce the oxidation rate, which made the Zr-doped, Pt-modified aluminide coating possess better oxidation resistance than the reference Pt-modified aluminide coating at the temperature of 1100 ◦C.
منابع مشابه
Nickel Base Superalloy Rene®80 – The Effect of High Temperature Cyclic Oxidation on Platinum-Aluminide Coating Features
Nickel base superalloy alloys are used in the manufacture of gas turbine engine components, which in use are exposed to high temperatures and corrosive environments. The platinum aluminide coatings described here have been developed to protect nickel base superalloy alloys from oxidation. In this study, the effect of cyclic oxidation, platinum layer thickness and aluminizing process on beha...
متن کاملFormation and Evaluation of Oxidation Behavior of Zirconia- Aluminide Coating on Nickel- Based Alloy
Practical applications of thermal barrier coatings with aluminide bond-coats are limited due to oxide scale spallation of the aluminide coating under applied thermal stresses. Considering the positive effects of oxygen-active elements or their oxides on the high temperature oxidation behavior, in this research zirconia was introduced into an aluminide coating. For this purpose, a Watts type bat...
متن کاملAluminide Coatings for Power Generation Applications
In order to form model aluminide coatings for studying critical issues related to their high temperature oxidation and corrosion performance, a laboratory chemical vapor deposition (CVD) procedure is being used to more rigorously control the coating process in terms of composition, purity and microstructure. One ferritic (Fe-9Cr1Mo) and one austenitic alloy (304L) were selected as substrate mat...
متن کاملRhodium and Hafnium Influence on the Microstructure, Phase Composition, and Oxidation Resistance of Aluminide Coatings
A 0.5 μm thick layer of rhodium was deposited on the CMSX 4 superalloy by the electroplating method. The rhodium-coated superalloy was hafnized and aluminized or only aluminized using the Chemical vapour deposition method. A comparison was made of the microstructure, phase composition, and oxidation resistance of three aluminide coatings: nonmodified (a), rhodium-modified (b), and rhodiumand ha...
متن کاملFormation Mechanism of Silicon Modified Aluminide Coating on a Ni-Base Superalloy
Formation mechanism of silicon modified aluminide coating applied on a nickel base super alloy IN-738 LC by pack cementation process was the subject of investigation in this research. Study of the microstructure and compositions of the coating was carried out, using optical and scanning electron microscopes, EDS and X-ray diffraction (XRD) techniques. The results showed that due to low partial ...
متن کامل