The Potential for the Improvement of High Performance Thermal Barrier Coatings
نویسنده
چکیده
The growing market for industrial gas turbines has led to an increased demand for large, cost-effective units of high efficiency, A critical issue in the development of such units is the durability of hot section components, especially first stage blades and vanes to which thermal barrier coatings (TBCs) are applied. This paper introduces the current state of the art in the production of TBCs, and discusses their various degradation mechanisms. Special emphasis is placed on the potential for the development of a new generation of TBC systems through the control of microstructure and porosity, as well as through new processing techniques.
منابع مشابه
Hot Corrosion Behavior of Functional Graded Material Thermal Barrier Coating (RESEARCH NOTE)
In this paper a functional graded material (FGM) thermal barrier coating (TBC) is prepared using Atmospheric Plasma Spraying (APS) method. The FGM layers were deposited by varying the feeding ratio of CYSZ/NiCrAlY and conventional CYSZ on a NiCrALY-coated Inconel 738 substrates. Hot corrosion behavior, bonding strength and the related failure mechanisms of a conventional TBC and a FGM TBC are i...
متن کاملA review of thermal barrier coating effects on diesel engine performance and components lifetime
In the present paper, a complete literatures review of thermal barrier coating applications in diesel engines is performed to select a proper type and to find coating effects. The coating system has effects on the fuel consumption, the power and the combustion efficiency, pollution contents and the fatigue lifetime of engine components. Usually there are several beneficial influences by appl...
متن کاملAN INVESTIGATION ON EFFECT OF BOND COAT REPLACEMENT ON HOT CORROSION PROPERTIES OF THERMAL BARRIER COATINGS
In the present study NiCrAlY bond coating layer was produced by electroplating against common atmospheric plasma spraying (APS). Both types of the bond coats were applied on IN738LC base metal then, the YSZ (ZrO2-8% Y2O3) thermal barrier top layer was coated by atmospheric plasma spray technique. Hot corrosion is one of the main destructive factors in thermal barrier coatings (TBCs) which come ...
متن کاملThe Study of High Temperature Oxidation behavior of Different Microstructures of HVOF Thermally Sprayed Coatings
Improvement of thermally sprayed coating properties by microstructure modification has been considered as a significant solution. Therefore, in this research the effect of dissolved oxygen content and post heat treatment on the formation and distribution of secondary phase particles, particularly in nano-scale in the coatings during spraying and after that were studied. Ni-5 wt% Al powders were...
متن کاملFailure Mechanisms Investigation in Thermal Barrier Coatings under Isothermal and Non-sothermal Fatigue Loadings using Design of Experiments
In this article, failure and fracture mechanisms in an aluminum alloy (which has been used in diesel internal combustion engines), with and without ceramic thermal barrier coatings, have been investigated under isothermal and non-isothermal fatigue loadings. In this research, the base material is an aluminum-silicon-magnesium alloy and the thermal barrier coating includes a metallic bond coat l...