Multichannel Mixed-Conducting Hollow Fiber Membranes for Oxygen Separation
نویسندگان
چکیده
A multichannel mixed-conducting hollow fiber (MMCHF) membrane, 0.5 wt % Nb2O5-doped SrCo0.8 Fe0.2O3-d (SCFNb), has been successfully prepared by phase inversion and sintering technique. The crystalline structure, morphology, sintering behavior, breaking load, and oxygen permeability of the MMCHF membrane were studied systematically. The MMCHF membrane with porous-dense asymmetrical microstructure was obtained with the outer diameter of 2.46 mm and inner tetra-bore diameter of 0.80 mm. The breaking load of the MMCHF membrane was 3–6 times that of conventional single-channel mixed-conducting hollow fiber membrane. The MMCHF membrane showed a high oxygen flux which was about two times that of symmetric capillary membrane at similar conditions as well as a good long-term stability under low oxygen partial pressure atmosphere. This work proposed a new configuration for the mixed-conducting membranes, combining advantages of multichannel tubular membrane technology and conventional hollow fibers. VC 2014 American Institute of Chemical Engineers AIChE J, 60: 1969–1976, 2014
منابع مشابه
CO2-tolerant mixed-conducting multichannel hollow fiber membrane for efficient oxygen separation
A mixed-conducting multichannel hollow fiber membrane (MCMHF) based on CO2-tolerant SrFe0.8Nb0.2O3–δ (SFN) oxide has been successfully prepared by phase inversion and sintering technique. The morphology, breaking load, oxygen permeability under CO2 atmosphere, thermal cycling performance and the long-term stability of the membrane were investigated in detail. The prepared membrane has a signifi...
متن کاملEnhanced High Oxygen Permeation of Mixed-Conducting Multichannel Hollow Fiber Membrane via Surface Modified Porous Layer
The oxygen permeation performance of Ba0.5Sr0.5Co0.8Fe0.2O3−δ (BSCF) mixed-conducting multichannel hollow fiber (MCMHF) membranes was improved by surface modification via spin-spraying of a La0.6Sr0.4CoO3−δ (LSC) porous layer. At 1173 K, the oxygen permeation flux of the modified membranes was clearly enhanced and reached 9.68 mL·cm−2·min−1, which is a remarkable high value in the field of mixe...
متن کاملA Robust Mixed-Conducting Multichannel Hollow Fiber Membrane Reactor
To accelerate the commercial application of mixed-conducting membrane reactor for catalytic reaction processes, a robust mixed-conducting multichannel hollow fiber (MCMHF) membrane reactor was constructed and characterized in this work. The MCMHF membrane based on reduction-tolerant and CO2-stable SrFe0.8Nb0.2O3-δ (SFN) oxide not only possesses a good mechanical strength, but also has a high ox...
متن کاملCO2‐Tolerant SrFe0.8Nb0.2O3−δ−Carbonate Dual-Phase Multichannel Hollow Fiber Membrane for CO2 Capture
Ceramic−carbonate dual-phase membranes have attracted a lot of attention because of the emission of CO2 and environmental problems. In this study, a dense SrFe0.8Nb0.2O3−δ−carbonate dual-phase multichannel hollow fiber membrane has been successfully prepared via a phase inversion−sintering technique and impregnation. The morphology, crystal structure, phase stability, breaking load, and CO2 per...
متن کاملMixed conducting ceramic membranes for high efficiency power generation with CO2 capture
Because of the emission of larger amount of CO2, power generation from fossil fuel has resulted in serious environmental problems. Integrating dense mixed-conducting membranes (MCMs) into power cycles with CO2 capture has been considered as the most advanced technology for high efficiency and clean power production. This paper presents an update of MCMs development efforts, including the recent...
متن کامل