Preparation and characterization of mesostructured polymer-functionalized sol–gel-derived thin films

The present study attempts to incorporate methacrylate-based polymers into ordered lamellar organic/inorganic nanocomposite films composed of alternating SiO2/polymer layers. The films are prepared by dip-coating from a solution containing the monomers and silica precursors, thus leading to composite lamellar mesostructured materials through evaporation-induced self-assembly (EISA). A polymerizable coupling agent is added to covalently link the polymers to the silica matrix. The final polymer/SiO2 hybrid material is obtained by a separate free-radical polymerization step, initiated by UV exposure or thermal treatment. Using trimethoxy(7-octen-1-yl)silane as a coupling agent, a procedure was established that preserved the mesostructure and maintained the swelling properties of the polymers, while acrylate-based coupling agents lead to a significant distortion of the film mesostructure. Structure and composition of the films were studied by X-ray diffraction, NMR and IR. © 2003 Published by Elsevier B.V.