Effect Of Na2o/Al2o3, Sio2/Al2o3 And W/B Ratio On Setting Time And Workability Of Flyash Based Geopolymer
نویسندگان
چکیده
The objectives of the present research is to appreciate the effect of synthesizing parameters on setting time and workability of Fly ash based geopolymer paste . Locally available low calcium fly ash from a thermal power plant located near Kolkata, India, was used . Fly ash used are lignite coal based and falls under class F category. The broad areas of present research include: Manufacturing of Geopolymer and a comprehensive study on the effect of synthesizing parameters , Alkali content (Na2O/Al2O3), Silica content (SiO2/Al2O3) and Water to Geopolymer binder ratio on setting time of geopolymer paste and workability of geopolymer mortar and arrived at certain level of understanding which will be useful to the researchers and
منابع مشابه
INVESTIGATING SHRINKAGE CHANGES OF NATURAL POZZOLAN BASED GEOPOLYMER CEMENTPASTE
Shrinkage behavior of a geopolymer cement paste prepared from pumice-type natural pozzolan was studiedby changing parameters of chemical composition including SiO2/Na2O molar ratio of activator and total molar ratiosof Na2O/Al2O3, and H2O/Al2O3. For investigating the effect of curing conditions on shrinkage, hydrothermal curingwas also applied. The obtained results clearly revealed the governin...
متن کاملModeling of Compressive Strength of Metakaolin Based Geopolymers by The Use of Artificial Neural Network RESEARCH NOTE)
In order to study the effect of R2O/Al2O3 (where R=Na or K), SiO2/Al2O3, Na2O/K2O and H2O/R2O molar ratios on the compressive strength (CS) of Metakaolin base geopolymers, more than forty data were gathered from literature. To increase the number of data, some experiments were also designed. The resulted data were utilized to train and test the three layer artificial neural network (ANN). Bayes...
متن کاملSynthesis of zeolite NaA nano-crystalls; effect of synthesis parameters on crystallinity and crystal size
Abstract In this work hydrothermal synthesis of zeolite NaA crystals with a composition of Al2O3:aSiO2:bNa2O:cH2O was investigated. Effects of SiO2/Al2O3, Na2O/Al2O3 and H2O/Al2O3 ratios and crystallization temperature and time were studied on crystallinity and crystal size of zeolite NaA crystals. It was tried to understand the interactions between these parameters. The crystal species o...
متن کاملEFFECT OF CALCINATION TEMPERATURE OF THE KAOLIN AND MOLAR Na2O/SiO2 ACTIVATOR RATIO ON PHYSICAL AND MICROSTRUCTURAL PROPERTIES OF METAKAOLIN BASED GEOPOLYMERS
Metakaolinite-based geopolymer has been synthesized at about 25 °C from metakaolin which has been calcined in different temperatures (600-900 °C) and different Na2O/SiO2 ratio activator (0.3-1.1). Compressive strength and microstructure of cement pastes after 7-28 days curing at ambient temperature were measured. Compressive strength tests on the samples showed that the sample made with calcine...
متن کاملEFFECT OF A FOURTH COMPONENT (Na2O, SrO, MgO AND BaO) ADDITION TO CaO-Al2O3-SiO2 SYNTHETIC SLAG ON SULFUR REMOVAL FROM PLAIN CARBON STEEL
In this paper, the effect of MgO, BaO, Na 2 O and SrO addition to a pre-melted CaO-Al2O3 -Si 2 O synthetic slag on sulfur removal from plain carbon steel was studied under the same experimental conditions. The slags were pre-melted at 1400°C in an electric resistant furnace and desulfurization experiments were carried out in a high frequency induction furnace. The results showed that ...
متن کامل