Thermal etching of GaAs(113) surfaces

نویسندگان

  • S. M. SCHOLZ
  • C. SETZER
  • K. JACOBI
  • J. P. RABE
چکیده

We discuss scanning electron micrographs and atomic force microscope images of thermally etched GaAs(113) surfaces. The GaAs(113)A and GaAs(113) B surfaces are compared. The polarity of the surface leads to a different morphology for the two surfaces after thermal etching. It is found that the Ga-enriched droplets, which form under As-deficient conditions at higher temperatures, are sitting on characteristic pedestals, which are different for the two faces. The facets occurring after this thermal etching process are identified. They represent thermally favourable surfaces under the arsenic-deficient conditions of the thermal etching process. © 1998 Chapman & Hall ________________________________________________________________________________________________

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Molecular beam epitaxy approach to the graphitization of GaAs„100... surfaces

The authors present a method for obtaining graphitized carbon on GaAs 100 surfaces. Carbon-doped GaAs is grown by molecular beam epitaxy before controlled thermal etching within the growth chamber. An AlAs layer beneath the carbon-doped GaAs acts as a thermal etch stop. As the GaAs is etched away, the carbon dopant atoms remain on the surface due to their low vapor pressure. The total number of...

متن کامل

Optimized cleaning method for producing device quality InP(100) surfaces

A very effective, two-step chemical etching method to produce clean InP(100) surfaces when combined with thermal annealing has been developed. The hydrogen peroxide/sulfuric acid based solutions, which are successfully used to clean GaAs(100) surfaces, leave a significant amount of residual oxide on the InP surface which can not be removed by thermal annealing. Therefore, a second chemical etch...

متن کامل

FLEXIBLE, THIN-FILM, GaAs HETERO-JUNCTION BIPOLAR TRANSISTORS MOUNTED ON NATURAL DIAMOND SUBSTRATES

Thermal considerations hecome important for optimal operation of high power heterojunction bipolar transistors (HBTs) in applications such as the next generation of phased-array radar systems. In particular, devices grown on GaAs substrates suffer due to the mediocre thermal conductivity of the III-V compound semiconductors. The maximum achievable power density before device performance degrade...

متن کامل

CH31 vapor etching of masked and patterned GaAs

CH3I vapor etching of masked and patterned GaAs substrates has been experimentally investigated. For GaAs samples masked with silicon nitride stripes that are wider than 30 tzm, the etch depth increased compared to unmasked samples, the magnitude of which increased with increasing mask width. Etching of bulk substrates of (l l l)Ga and (lll)As GaAs revealed a dependence of etch rate on crystal ...

متن کامل

Damage-free top-down processes for fabricating two-dimensional arrays of 7 nm GaAs nanodiscs using bio-templates and neutral beam etching.

The first damage-free top-down fabrication processes for a two-dimensional array of 7 nm GaAs nanodiscs was developed by using ferritin (a protein which includes a 7 nm diameter iron core) bio-templates and neutral beam etching. The photoluminescence of GaAs etched with a neutral beam clearly revealed that the processes could accomplish defect-free etching for GaAs. In the bio-template process,...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 1999