The frictional properties of thin inorganic halide films on iron measured in ultrahigh vacuum
نویسندگان
چکیده
Friction coefficients are measured in ultrahigh vacuum using a tungsten carbide tribopin against thin films of sodium chloride and potassium iodide deposited onto clean iron. It is found, in accordance with previous measurements for potassium chloride on iron, that the friction coefficient falls from an initial value of 2 for the clean iron surface to a minimum value after a few tens of Ångstroms of the halide have been deposited onto the surface, and remains constant for thicker films. The minimum friction coefficient is independent of applied load and therefore obeys Amontons’ law. Simple theories for the effect of a low-shear-strength film suggest that the friction coefficient should depend on the shear strength of the film. This idea is tested by plotting the minimum friction coefficient versus the hardness of the film material, which is proportional to its shear strength, where a linear correlation was found. The lack of dependence of friction coefficient with film thickness for thicker films implies that ploughing forces do not contribute significantly to the friction coefficient.
منابع مشابه
The friction, mobility and transfer of tribological films: potassium chloride and ferrous chloride on iron
The tribological properties of FeCl2, measured using an ultrahigh vacuum tribometer, are compared with those of KCl. The friction coefficient of an FeCl2 film evaporated onto iron in ultrahigh vacuum decreases to ∼0.08 after the deposition of a film ∼40 Å thick. This value is in good agreement with that measured for reactively formed FeCl2 films in a pin and v-block apparatus. The contact resis...
متن کاملStructural Properties of Post Annealed ITO Thin Films at Different Temperatures
Indium tin oxide (ITO) thin films were deposited on glass substrates by RF sputtering using an ITO ceramic target (In2O3-SnO2, 90-10 wt. %). After deposition, samples were annealed at different temperatures in vacuum furnace. The post vacuum annealing effects on the structural, optical and electrical properties of ITO films were investigated. Polycrystalline...
متن کاملLongitudinal Magneto-Optical Kerr Effect in Ce:YIG Thin Films Incorporating Gold Nanoparticles
We report an experimental study on optical and magneto-optical properties of Cesubstituted yttrium iron garnet thin films incorporating gold nanoparticles. Au nanoparticles were formed by heating Au thin film on cubic quartz and garnet substrate in vacuum chamber and a Ce:YIG layer was deposited on them by the aid of Pulsed laser deposition method. A large enhancement of the longitudinal Kerr e...
متن کاملThe tribological properties of monolayer KCl films on iron in ultrahigh vacuum: Modeling the extreme-pressure lubricating interface
The friction coefficients of thin KCl films deposited onto clean iron in ultrahigh vacuum are measured using a tungsten carbide tip. A rapid decrease is found in the friction coefficient from 2 for clean iron to 0:27 0:03 after the deposition of 40 A of KCl. Based on previous contact resistance measurements, this was proposed to be due to the completion of the first layer of KCl. The firstlayer...