Stoichiometric hydroxyapatite obtained by precipitation and sol gel processes
نویسندگان
چکیده
Se describen tres métodos para obtener hidroxiapatita (HA). La HA es una cerámica muy interesante por sus múltiples aplicaciones médicas. Los primeros dos métodos de precipitación parten de compuestos de calcio y fósforo, mientras que el tercer método es un proceso sol-gel que usa alcóxidos. Los productos fueron caracterizados y comparados entre sı́. Las diferencias observadas son importantes para aplicaciones prácticas.
منابع مشابه
Deposition of Nano-Crystalline Fluor-hydroxyapatite Coatings on Titanium Substrates via Sol-Gel Method
In this investigation, fluor-hydroxyapatite (FHA) film was deposited on a titanium substrate by sol-gel method. Triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol solutions were used respectively as P, F and Ca precursors. Typical apatite structures were obtained for all coatings after dipping and subsequent heat treatment at 550, 700 and 800 ºC, the coating layers were ...
متن کاملSynthesis and Structural Analysis of Sol Gel Derived Stoichiometric Monophasic Hydroxyapatite
Hydroxyapatite (HAP) ceramics belongs to a class of calcium phosphate-based biomaterial, which has been widely used as bone substitute for long time. In recent years, synthetic HAP has assumed substantial interest and importance due to its chemical similarity with the natural Ca phosphate mineral present in a biological hard tissue. Considering the wide applications of calcium phosphate compoun...
متن کاملCrystallization Kinetics of Hydroxyapatite Nano-films on Stainless Steel Through a Sol-Gel Process
This article describes the preparation and analysis of nano hydroxyapatite (HA) films on stainless steel 316L through sol-gel technique. The process started with preparation of a nitrate and phosphate sol. After aging the sol for 24 h at room temperature a SS316 substrate was dip-coated and heat-treated at 350 to 450 °C for different times in air. The coating phase and structure on subs...
متن کاملSol-gel synthesis of FHA / CDHA nanoparticles with a nonstochiometric ratio
The aim of this study was to investigate the sol gel synthesis of HA/FA nanoparticles and the possible formation of TCP phase or unstoichiometric calcium deficient hydroxyapatite (CDHA) from the precursors with a Ca/P ratio of 1.62. In order to prepare the sol, the solutions of Triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol were used respectively as P, F and Ca precursors....
متن کاملSol-gel synthesis of FHA / CDHA nanoparticles with a nonstochiometric ratio
The aim of this study was to investigate the sol gel synthesis of HA/FA nanoparticles and the possible formation of TCP phase or unstoichiometric calcium deficient hydroxyapatite (CDHA) from the precursors with a Ca/P ratio of 1.62. In order to prepare the sol, the solutions of Triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol were used respectively as P, F and Ca precursors....