Immediate and Delayed Solubility of Mineral Trioxide Aggregate and Portland Cement
نویسندگان
چکیده
This study investigated the solubility of mineral trioxide aggregate (MTA) and Portland cement since its mixture until 672 hours, by means of two complimentary methods. Metal ring molds filled with the cements were covered with distilled water and, at each experimental time (3, 24, 72, 168, 336 and 672 hours), were weighed as soon as the plates in which the samples have been placed. Empty rings served as the control group (n=8). Mean weight gain and loss was determined and analyzed statistically by two-way ANOVA and Tukey's test for all pairwise comparisons. Only Portland cement showed less than 3% weight loss through 24 hours. Detached MTA residues were heavier than those of Portland cement over the 3 to 168 hours. The weight of MTA rings increased more than that of Portland rings within 672 hours (p=0.05). The findings of the present study indicate that, in an aqueous environment MTA is more soluble than Portland cement and exceeds the maximum weight loss considered acceptable by ISO 6876 standard (2001).
منابع مشابه
Physical evaluation of a new pulp capping material developed from portland cement
BACKGROUND This study examined the effects of addition of 10% and 25% by weight calcium hydroxide on the physicochemical properties of Portland cement associated with 20% bismuth oxide in order to develop a new pulp capping material. MATERIAL AND METHODS The solubility, pH value, setting time, compressive strength, and push out bond strength of modified Portland were evaluated and compared to...
متن کاملOne-year outcomes of MTA and modified Portland cement pulpotomy in primary teeth: a randomized clinical trial
Purpose: To compare the efficacy of Mineral Trioxide Aggregate (MTA) and Modified Portland Cement (MPC) as pulpotomy medicaments in primary molars. Methods: A sample of 54 children 4 to 6 years old of age, who had at least one primary mandibular second molar that needed pulpotomy were randomly placed in MTA (n = 28) or MPC (n = 26) groups. After completing the pulpotomy procedures, the teeth ...
متن کاملMineral Trioxide Aggregate and Portland Cement for Direct Pulp Capping in Dog: A Histopathological Evaluation
Background and aims. Mineral trioxide aggregate and calcium hydroxide are considered the gold standard pulp-capping materials. Recently, Portland cement has been introduced with properties similar to those of mineral trioxide aggregate. Histopathological effects of direct pulp capping using mineral trioxide aggregate and Portland cements on dog dental pulp tissue were evaluated in the present s...
متن کاملPortland cement versus MTA as a root-end filling material. A pilot study.
PURPOSE To assess periradicular lesions clinically and by computed tomography (CT) after endodontic surgery using either Portland cement or mineral trioxide aggregate (MTA) as a root-end filling material. METHODS Three patients diagnosed with periradicular lesions by cone-beam CT underwent endodontic surgery with root-end filling. Patient A was treated with MTA as the root-end filling materia...
متن کاملSetting expansion of gray and white mineral trioxide aggregate and Portland cement.
One possible reason for the sealing ability of mineral trioxide aggregate (MTA) is its slight expansion upon setting. Both gray mineral trioxide aggregate (GMTA) and white mineral trioxide aggregate (WMTA) are composed of approximately 75% Portland cement (PC). WMTA differs from GMTA in its lower content of tetracalcium aluminoferrite. This difference in composition may affect setting expansion...