Anneal-Hardening Behavior of Cr-Fe-C Alloy Deposits Prepared in a Cr3+-Based Bath with Fe2+ Ions
نویسندگان
چکیده
Cr-Fe-C alloy deposits were successfully prepared on high-carbon tool steel in a Cr3+-based electroplating bath containing Fe2+ ions and suitable complex agents. A Cr-based alloy deposit was obtained with an electroplating current density higher than 25 Adm-2, and a Fe-based alloy deposit was obtained using a current density of 20 Adm-2. Following electroplating, these alloy deposited specimens were annealed via rapid thermal annealing (RTA) at 500 °C for different periods up to 30 s. The experimental results show that Cr- and Fe-based alloy deposits could be significantly hardened after RTA at 500 °C for a few seconds. The maximum hardness was that of the Cr-Fe-C alloy deposit annealed at 500 °C for 10 s. The maximum hardness of 1205 Hv was detected from the annealed Cr-based alloy deposit prepared with 30 ASD. The hardening mechanism of annealed Cr- and Fe-based alloy deposits is attributed to the precipitation of C-related membranes. The hardness values of the annealed Cr- and Fe-based alloy deposits increase with the increasing degree of crystallization of the C-related membranes.
منابع مشابه
Surface Chemistry and Spectroscopy of Chromium in Inorganic Oxides.
A. General Introduction Among the transition metal ions of the 3d series, Cr takes a particular position because of its variability in oxidation state, coordination numbers and molecular structure.1,2 The elucidation of these Cr species on inorganic oxidic surfaces is a complex task, which is of fundamental importance to understanding the behavior of Cr in the environment, colloids, and Cr-base...
متن کاملEffective Removal of Heavy Metal Ions Zn2+, Ni2+, Cu2+, Cr3+ from Aqueous Solution by Synthetic Superabsorbent Polymer
Heavy metal pollution is propagating throughout the world with the enlargement of industrial activities. The elimination of heavy metal ions from industrial wastewaters has drawn much attention because of the hazardous effects of the heavy metal ions on different organisms. According to these facts, poly (2, 2, 3, 3- tetracyanocyclopropyl) phenyl acryl...
متن کاملMineralogical and geochemical investigations of chromite ores from ophiolite complexes of SE Iran in terms of chrome spinel composition
Ten chromite ores from ophiolite complexes in SE Iran were analyzed mineralogically by XRD, chemically by XRF, and mineral chemistry by EPMA. The identified paragenesis of silicate minerals of chromite ores with the X-ray diffraction is pronounced differently. It consists of secondary phases formed as serpentine, Cr-containing chlorite (kaemmererite), chromic garnet (uarovite) with preserved pa...
متن کاملELECTRODEPOSITION OF Ni-Fe ALLOYS FROM SULFATE, SULFATE-CHLORIDE AND CHLORIDE BATHS
In an attempt to control the film composition, factors affecting the composition of Ni-Fe alloy deposits and their crystal structure have been analyzed as a function of bath composition, cathode current density, bath pH, temperature and an addition of citric acid. antimony electrode revealed that the deposition potential of Fe coincides with the potential where the abrupt increase of pH was obs...
متن کاملSURFACE HARDENING OF TUNGSTEN-BASED HEAVY ALLOY VIA PACK BORONIZING
The boronizing of a tungsten heavy alloy containing Ni and Fe as the major alloying elements were performed in the present study to increase its surface hardening. Pack cementation method was employed as a well-known, successful solid-state process for boronizing. The coating treatment was accomplished at different temperatures of 1000, 1050 and 1100°C for 6 and 9 hours. The formation of tu...
متن کامل